The invention relates to a thick gold refining method, the specific steps are as follows: (1) thick gold with nitric acid digestion solution, filtering residue I; (2) adding potassium nitrate in residue I, after mixing by roasting roasting slag; (3) adding potassium hydroxide in boiling roasting slag, filtering residue II; (4) the residue of nitric acid digestion, filtration to obtain filter residue III; (5) in residue III adding hydrochloric acid and hydrogen peroxide reaction, filtering to obtain filtrate to obtain gold powder. Using the method of refined gold powder purity above 99.99%, this method overcomes the fire wet method combined with the purity of products is not high, high melting temperature, complex process and long period of weakness.
【技术实现步骤摘要】
一种粗金精炼方法
本专利技术属于冶金
，涉及一种粗金精炼技术。
技术介绍
黄金是人类较早发现和利用的金属，由于稀少、特殊和珍贵，自古以来被视为五金之首，有金属之王的称号。它具有极高的抗腐蚀的稳定性，良好的导电性和导热性，金的原子核具有较大捕抓中子的有效截面，在金的合金中具有各种触媒性质。目前精炼的主要方法有电解法、萃取法、全湿法精炼、湿法-火法联用精炼。电解法精炼的基本原理是：以粗金做阳极，在直流电作用下，金与其它更电负性金属以离子形式进入电解液，因为金离子浓度大，电位高，金率先在阴极得电子析出，使粗金得到提纯。电解法所得黄金纯度在99.99％以上，且质量较稳定，但是电解工艺存在如下缺点：对原料要求高(一般要求粗金品位在90％以上)；技术条件要求较高；生产周期长；流程中积压大量黄金，对资金周转及安全保卫工作带来不便。萃取法相对电解工艺具有生产周期短、流程不积压黄金、直收率高、操作简单的优势，但是萃取法的不足也是相当明显：萃取工艺的萃取剂的选择性不大，而且萃取法试剂消耗大，生产对环境造成的污染较大，劳动环境差，废气治理困难，萃取法一般要求原料的金含量达到80-...
【技术保护点】
一种粗金精炼方法，其特征在于，包括如下步骤：(1)粗金用硝酸溶液浸煮，过滤，得到滤渣Ⅰ；(2)在滤渣Ⅰ中加入硝酸钾，混匀后焙烧，得到焙烧渣；(3)将焙烧渣加入氢氧化钾溶液浸煮，过滤得到滤渣Ⅱ；(4)将滤渣Ⅱ用硝酸浸煮，过滤，得到滤渣Ⅲ；(5)在滤渣Ⅲ加入盐酸和双氧水反应，过滤得到滤液；处理，得到金粉。
【技术特征摘要】
1.一种粗金精炼方法，其特征在于，包括如下步骤：(1)粗金用硝酸溶液浸煮，过滤，得到滤渣Ⅰ；(2)在滤渣Ⅰ中加入硝酸钾，混匀后焙烧，得到焙烧渣；(3)将焙烧渣加入氢氧化钾溶液浸煮，过滤得到滤渣Ⅱ；(4)将滤渣Ⅱ用硝酸浸煮，过滤，得到滤渣Ⅲ；(5)在滤渣Ⅲ加入盐酸和双氧水反应，过滤得到滤液；处理，得到金粉。2.根据权利要求1所述的粗金精炼方法，其特征在于，步骤(1)中，所述硝酸的质量百分数为15-30％，粗金与硝酸溶液的重量体积比为1:1-3。3.根据权利要求1所述的粗金精炼方法，其特征在于，步骤(2)中，所述焙烧的温度为450-600℃。4.根据权利要求1所述的粗金精炼方法，其特征在于，步骤(2)中，硝酸钾用量为滤渣Ⅰ重量的10％-40％。5.根据权利要求1所述的粗金精炼方法，其特征在于，步骤(3)中，所述的氢氧化钾溶液的质量百...
【专利技术属性】
技术研发人员：陈兰，粟明辉，黄鹏飞，李环，杨跃新，
申请(专利权)人：郴州市金贵银业股份有限公司，
类型：发明
国别省市：湖南,43
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。