基于可充放气/液芯轴套的编织纤维增强结构件制造方法技术
Method of manufacturing a woven fiber reinforced structural member based on a charge deflation / liquid core shaft
The invention relates to a woven fabric can be inflated or deflated / liquid core shaft based on enhanced structure manufacturing method, which comprises the following steps: 1), flexible mandrel preparation; 2), inflatable molding; 3), 4), curing and weaving; modulus. The invention of the woven fabric can be inflated or deflated / liquid core shaft based on enhanced structure manufacturing method comprises a flexible mandrel preparation and special composite structures of flexible shaft based on the preparation of fiber reinforced, high production efficiency, low manufacturing cost advantages.
【技术实现步骤摘要】
基于可充放气/液芯轴的编织纤维增强结构件制造方法
本专利技术涉及一种异型中空结构件的制造方法，具体涉及一种基于可充放气/液芯轴的编织纤维增强结构件制造方法，属于纺织机械
技术介绍
环形编织工艺是制备中空纤维增强复合材料结构件的主要方式。在这种制造方法中，增强纤维将首先被编织到具有特定形状的芯轴上，在编织物上注入树脂之后并固化成型之后，将芯轴抽出，最后获得中空复合材料结构件。对于等截面的规则结构件，可以通过非破坏的方式将芯轴取出，使芯轴能够被重复使用。然而，对于非规则的异型结构件，就需要使用特殊材料（如蜡、沙、或是可溶解的高分子聚合物）制作芯轴，在完成结构件的产生之后，通过相应方式将固结的芯轴分解破坏，这样将会增长生产周期和抬高制造成本。因此，为解决上述技术问题，确有必要提供一种创新的基于可充放气/液芯轴的编织纤维增强结构件制造方法，以克服现有技术中的所述缺陷。
技术实现思路
为解决上述技术问题，本专利技术的目的在于一种生产效率高，制造成本低的基于可充放气/液芯轴的编织纤维增强结构件制造方法，其包括了纤维增强的柔性芯轴制备及基于柔性芯轴的异型复合材...
【技术保护点】
基于可充放气/液芯轴的编织纤维增强结构件制造方法，其特征在于：包括如下工艺步骤：1），进行柔性芯轴的制备；2），充气成型；3），编织；4），固化和取模。
【技术特征摘要】
1.基于可充放气/液芯轴的编织纤维增强结构件制造方法，其特征在于：包括如下工艺步骤：1），进行柔性芯轴的制备；2），充气成型；3），编织；4），固化和取模。2.如权利要求1所述的基于可充放气/液芯轴的编织纤维增强结构件制造方法，其特征在于：所述步骤1）具体为：1-1），采用编织机将高强低弹的纤维致密包缠到芯轴内模表面；1-2），将编织后的芯轴内模放入到乳胶浸润设备；1-3），将浸润乳胶去除芯轴内模后制备的柔性芯轴套。3.如权利要求2所述的基于可充放气/液芯轴的编织纤维增强结构件制造方法，其特征在于：所述芯轴内模的一端设置有充气/液接口；所述纤维全部连接在充气/液接口上，再在芯轴内模上编制纤维增强体。4.如权利要求1所述的基于可充放气/液芯轴的编织纤维增强结构件制造方法，其特征在于：所述步骤2）具体为：2-1），在柔性芯轴上安装轴充气/液接头；2-2），使用充气/液设备，从进气口对其充气/液，使之硬化定型从而形成编织芯轴。5.如权利要求4所述的基于可充放气/液芯轴的编织纤维增强结构件制造方法，其特征在于：所述充气/液接头螺接至芯轴的充气/液接口上，...