The present invention provides a method for preparing flame retardant rigid polyurethane foam, the polyether polyol, foaming agent, foam stabilizer, amine catalyst, methyl phosphonic acid, glycerol, urea, two methyl cellulose, citric acid, silica sol mixture, 200 300rpm dispersion, then adding polymethylene polyphenyl isocyanate, dispersion the resulting mixture, add to the mold, static foaming, curing, demoulding to obtain the flame retardant rigid polyurethane foam. In order to solve the technical problem of poor flame retardancy of the existing rigid polyurethane foam plastics, citric acid is added into the preparation process of the rigid polyurethane foam and is adopted in the CO
【技术实现步骤摘要】
一种阻燃硬质聚氨酯泡沫塑料的制备方法
本专利技术属于建筑材料
，具体涉及一种阻燃硬质聚氨酯泡沫塑料的制备方法。
技术介绍
目前我国建筑能耗已占到全社会总能耗的1/3，且仍以每年1%的速度在增长，建筑节能已经成为国家的一项基本国策。我国建筑总面积约为400亿平方米，高能耗建筑占到了95%以上，这是造成我国建筑能耗较高的主要原因。通过墙体、管道、屋顶等传热是建筑物耗能的主要途径，而应用优异保温材料的建筑物能显著减少采暖制冷所造成的能量损耗，是减少建筑能耗的关键。硬质聚氨酯泡沫塑料的导热系数是所有有机保温材料中最低的，具有极佳的隔热保温性能。在欧美等一些发达国家，聚氨酯硬泡在墙体保温材料所占市场份额已经在50%以上，而目前我国聚氨酯保温材料的使用率还不到10%。虽然聚氨酯硬泡有着优异的保温性能，但未经阻燃处理的硬泡氧指数只有16%~18%，极易燃烧，且在燃烧过程中释放出大量有毒烟雾，对人们的生命财产安全造成极大威胁。因此，研究制备新型环保阻燃硬质聚氨酯泡沫塑料具有非常重要的现实意义。
技术实现思路
解决的技术问题：为了解决现有硬质聚氨酯泡沫塑料阻燃性差的技术问题，在硬...
【技术保护点】
一种阻燃硬质聚氨酯泡沫塑料的制备方法，其特征在于：包括以下步骤：步骤1，以重量份计，将聚醚多元醇90‑120份、发泡剂0.5‑1.2份、胺类催化剂0.8‑1.8份、泡沫稳定剂0.5‑1.2份、甘油0.02‑0.05份、甲基膦酸二甲酯0.1‑0.4份、尿素2.4‑4.5份、纤维素0.2‑0.6份、柠檬酸0.01‑0.05份、硅溶胶0.02‑0.07份混合，200‑300rpm分散10‑15min，得到混合物A；步骤2，以重量份计，将多亚甲基多苯基异氰酸酯115‑140份加至混合物A中，700‑800rpm分散30‑40s，得到混合物B；步骤3，将混合物B加至模具中，静置发泡，...
【技术特征摘要】
1.一种阻燃硬质聚氨酯泡沫塑料的制备方法，其特征在于：包括以下步骤：步骤1，以重量份计，将聚醚多元醇90-120份、发泡剂0.5-1.2份、胺类催化剂0.8-1.8份、泡沫稳定剂0.5-1.2份、甘油0.02-0.05份、甲基膦酸二甲酯0.1-0.4份、尿素2.4-4.5份、纤维素0.2-0.6份、柠檬酸0.01-0.05份、硅溶胶0.02-0.07份混合，200-300rpm分散10-15min，得到混合物A；步骤2，以重量份计，将多亚甲基多苯基异氰酸酯115-140份加至混合物A中，700-800rpm分散30-40s，得到混合物B；步骤3，将混合物B加至模具中，静置发泡，熟化，脱模后即得所述阻燃硬质聚氨酯泡沫塑料。2.根据权利要求1所述的阻燃硬质聚氨酯泡沫塑料的制备方法，其特征在于：所述聚醚多元醇的平均官能度为4.7-5.0，羟值为430-470mgKOH/g，粘度...