本发明专利技术公开了一种耐腐蚀钼钒合金钢及其在钻进钻杆中的应用，其化学成分及质量百分比为：碳0.38～0.46％，钼7.6～8.4％，钒2.8～3.6％，镍1.1～1.5％，硅0.9～1.5％，铼0.06～0.10％，锰0.8～1.4％，钴0.07～0.09％，磷0.013～0.017％，铬0.44～0.62％，硫0.04～0.08％，铷0.09～0.15％，锶0.02～0.04％，镓0.014～0.018％，钛和锆共0.04～0.06％，钛和锆所占质量百分比的比例为3～5:1，其余为铁。本发明专利技术提供的钼钒基合金钢材料耐腐蚀性能优异，适合用于制备钻进钻杆。
Corrosion resisting molybdenum vanadium alloy steel and application thereof in drilling rod
The invention discloses a corrosion resistant molybdenum vanadium alloy steel and its application in the drill pipe in the drilling, the chemical constituents and quality percentage: carbon 0.38 ~ 0.46%, 7.6 ~ 8.4% Mo, V 2.8 ~ 3.6%, 1.1 ~ 1.5% Ni Si 0.9 ~ 1.5%, 0.06 ~ 0.10%, rhenium from 0.8 to 1.4%, manganese, cobalt 0.07 ~ 0.09%, 0.013 ~ 0.017% P, Cr 0.44 ~ 0.62%, sulfur 0.04 ~ 0.08%, 0.09 ~ 0.15% Rb, Sr 0.02 ~ 0.04%, 0.014 ~ 0.018% GA, titanium and zirconium were 0.04 ~ 0.06%, titanium and zirconium the percentage proportion is 3 ~ 5:1, the rest is iron. The molybdenum vanadium alloy steel material provided by the invention has excellent corrosion resistance and is suitable for preparing a drilling rod.
【技术实现步骤摘要】
一种耐腐蚀钼钒合金钢及其在钻进钻杆中的应用
本专利技术属于钻杆领域，具体涉及一种耐腐蚀钼钒合金钢及其在钻进钻杆中的应用。
技术介绍
钢是铁碳合金的统称。在实际生产中，钢往往根据用途的不同含有不同的合金元素，人类对钢的应用和研究历史相当悠久，但是直到19世纪贝氏炼钢法专利技术之前，钢的制取都是一项高成本低效率的工作。如今，钢以其低廉的价格、可靠的性能成为世界上使用最多的材料之一，是建筑业、制造业和人们日常生活中不可或缺的成分。可以说钢是现代社会的物质基础。但是钢本身特性存在缺点，密度高，比较重，比较易被腐蚀，比较脆容易断裂。实际应用中，钻进钻杆用钢需要具有较高的耐腐蚀性能。
技术实现思路
本专利技术的目的在于提供一种耐腐蚀钼钒合金钢及其在钻进钻杆中的应用。本专利技术的上述目的是通过下面的技术方案得以实现的：一种耐腐蚀钼钒合金钢，其化学成分及质量百分比为：碳0.38～0.46％，钼7.6～8.4％，钒2.8～3.6％，镍1.1～1.5％，硅0.9～1.5％，铼0.06～0.10％，锰0.8～1.4％，钴0.07～0.09％，磷0.013～0.017％，铬0.44～0.62％，硫0.04～0.08％，铷0.09～0.15％，锶0.02～0.04％，镓0.014～0.018％，钛和锆共0.04～0.06％，钛和锆所占质量百分比的比例为3～5:1，其余为铁。进一步地，所述耐腐蚀钼钒合金钢化学成分及质量百分比为：碳0.42％，钼8.0％，钒3.2％，镍1.3％，硅1.2％，铼0.08％，锰1.1％，钴0.08％，磷0.015％，铬0.53％，硫0.06％，铷0.12％，锶0.03％，镓0.016％，钛和锆共0.05％，钛和锆质量百分比的比例为4:1，其余为铁。进一步地，所述耐腐蚀钼钒合金钢化学成分及质量百分比为：碳0.38％，钼7.6％，钒2.8％，镍1.1％，硅0.9％，铼0.06％，锰0.8％，钴0.07％，磷0.013％，铬0.44％，硫0.04％，铷0.09％，锶0.02％，镓0.014％，钛和锆共0.04％，钛和锆所占质量百分比的比例为3:1，其余为铁。进一步地，所述耐腐蚀钼钒合金钢化学成分及质量百分比为：碳0.46％，钼8.4％，钒3.6％，镍1.5％，硅1.5％，铼0.10％，锰1.4％，钴0.09％，磷0.017％，铬0.62％，硫0.08％，铷0.15％，锶0.04％，镓0.018％，钛和锆共0.06％，钛和锆所占质量百分比的比例为5:1，其余为铁。上述耐腐蚀钼钒合金钢在制备钻进钻杆中的应用。本专利技术的优点：本专利技术提供的钼钒基合金钢材料耐腐蚀性能优异，适合用于制备钻进钻杆。具体实施方式下面结合实施例进一步说明本专利技术的实质性内容，但并不以此限定本专利技术保护范围。尽管参照较佳实施例对本专利技术作了详细说明，本领域的普通技术人员应当理解，可以对本专利技术的技术方案进行修改或者等同替换，而不脱离本专利技术技术方案的实质和范围。实施例1：钼钒基合金钢材料化学成分及质量百分比为：碳0.42％，钼8.0％，钒3.2％，镍1.3％，硅1.2％，铼0.08％，锰1.1％，钴0.08％，磷0.015％，铬0.53％，硫0.06％，铷0.12％，锶0.03％，镓0.016％，钛和锆共0.05％，钛和锆所占质量百分比的比例为4:1，其余为铁。实施例2：钼钒基合金钢材料化学成分及质量百分比为：碳0.38％，钼7.6％，钒2.8％，镍1.1％，硅0.9％，铼0.06％，锰0.8％，钴0.07％，磷0.013％，铬0.44％，硫0.04％，铷0.09％，锶0.02％，镓0.014％，钛和锆共0.04％，钛和锆所占质量百分比的比例为3:1，其余为铁。实施例3：钼钒基合金钢材料化学成分及质量百分比为：碳0.46％，钼8.4％，钒3.6％，镍1.5％，硅1.5％，铼0.10％，锰1.4％，钴0.09％，磷0.017％，铬0.62％，硫0.08％，铷0.15％，锶0.04％，镓0.018％，钛和锆共0.06％，钛和锆所占质量百分比的比例为5:1，其余为铁。实施例4：钼钒基合金钢材料化学成分及质量百分比为：碳0.42％，钼8.0％，钒3.2％，镍1.3％，硅1.2％，铼0.08％，锰1.1％，钴0.08％，磷0.015％，铬0.53％，硫0.06％，铷0.12％，锶0.03％，镓0.016％，钛和锆共0.05％，钛和锆所占质量百分比的比例为3:1，其余为铁。实施例5：钼钒基合金钢材料化学成分及质量百分比为：碳0.42％，钼8.0％，钒3.2％，镍1.3％，硅1.2％，铼0.08％，锰1.1％，钴0.08％，磷0.015％，铬0.53％，硫0.06％，铷0.12％，锶0.03％，镓0.016％，钛和锆共0.05％，钛和锆所占质量百分比的比例为5:1，其余为铁。实施例6：对比实施例化学成分及质量百分比为：碳0.42％，钼8.0％，钒3.2％，镍1.3％，硅1.2％，铼0.08％，锰1.1％，钴0.08％，磷0.015％，铬0.53％，硫0.06％，铷0.12％，锶0.03％，镓0.016％，钛和锆共0.05％，钛和锆所占质量百分比的比例为2:1，其余为铁。实施例7：对比实施例化学成分及质量百分比为：碳0.42％，钼8.0％，钒3.2％，镍1.3％，硅1.2％，铼0.08％，锰1.1％，钴0.08％，磷0.015％，铬0.53％，硫0.06％，铷0.12％，锶0.03％，镓0.016％，钛和锆共0.05％，钛和锆所占质量百分比的比例为6:1，其余为铁。实施例8：效果实施例对制备得到的实施例1～7的合金钢进行了耐腐蚀测试。将实施例1～7的钢材料分别放入5wt％的NaCl溶液、10wt％的硫酸溶液和10wt％的氢氧化钾溶液中，测定时间为1年。结果见下表。5wt％的NaCl溶液10wt％的硫酸溶液10wt％的氢氧化钾实施例10.0002mm/年0.001mm/年0.001mm/年实施例40.0002mm/年0.001mm/年0.001mm/年实施例50.0002mm/年0.001mm/年0.001mm/年实施例60.0010mm/年0.013mm/年0.009mm/年实施例70.0012mm/年0.015mm/年0.013mm/年实施例2、3测试结果与实施例4、5基本一致。本专利技术提供的钼钒基合金钢材料耐腐蚀性能优异，适合用于制备钻进钻杆。上述实施例的作用在于说明本专利技术的实质性内容，但并不以此限定本专利技术的保护范围。本领域的普通技术人员应当理解，可以对本专利技术的技术方案进行修改或者等同替换，而不脱离本专利技术技术方案的实质和保护范围。本文档来自技高网...
【技术保护点】
一种耐腐蚀钼钒合金钢，其特征在于，其化学成分及质量百分比为：碳0.38～0.46％，钼7.6～8.4％，钒2.8～3.6％，镍1.1～1.5％，硅0.9～1.5％，铼0.06～0.10％，锰0.8～1.4％，钴0.07～0.09％，磷0.013～0.017％，铬0.44～0.62％，硫0.04～0.08％，铷0.09～0.15％，锶0.02～0.04％，镓0.014～0.018％，钛和锆共0.04～0.06％，钛和锆所占质量百分比的比例为3～5:1，其余为铁。
【技术特征摘要】
1.一种耐腐蚀钼钒合金钢，其特征在于，其化学成分及质量百分比为：碳0.38～0.46％，钼7.6～8.4％，钒2.8～3.6％，镍1.1～1.5％，硅0.9～1.5％，铼0.06～0.10％，锰0.8～1.4％，钴0.07～0.09％，磷0.013～0.017％，铬0.44～0.62％，硫0.04～0.08％，铷0.09～0.15％，锶0.02～0.04％，镓0.014～0.018％，钛和锆共0.04～0.06％，钛和锆所占质量百分比的比例为3～5:1，其余为铁。2.根据权利要求1所述的耐腐蚀钼钒合金钢，其特征在于，化学成分及质量百分比为：碳0.42％，钼8.0％，钒3.2％，镍1.3％，硅1.2％，铼0.08％，锰1.1％，钴0.08％，磷0.015％，铬0.53％，硫0.06％，铷0.12％，锶0.03％，镓0.016％，钛和锆共0.05％，钛和锆所占质...
【专利技术属性】
技术研发人员：吴舒晨，
申请(专利权)人：吴舒晨，
类型：发明
国别省市：浙江,33