The invention discloses a preparation method of environmental protection plant straw brick, which comprises the following steps: firstly, according to the weight ratio of the following raw materials: Cement Concrete 10 14, 6 10 plant straw powder, flame retardant, curing agent 1 2 3 5; the cement concrete, plant straw powder, flame retardant agent, curing agent, mixing, a brick mold, standing 2 5 hours; the air is heated to 50 DEG C for 10 100, 28min, cooling to room temperature. The invention adopts conventional materials effectively, a brick raw material, after mixing, injection molding, static, heating and cooling, can obtain the brick; product is light weight, strength, good stability; good environmental performance, is a new environmental protection material.
【技术实现步骤摘要】
植物秸秆环保砖的制备方法
本专利技术涉及炭化
,尤其是一种植物秸秆环保砖的制备方法。
技术介绍
植物秸秆是农作物的副产物,产量巨大,用途只要体现在以下几个方面,可以做成秸秆颗粒燃料,这比较大的用量;二是做成秸秆砖供应养牛专业户或出口缺乏资源的国家;三是也可以自己进行微贮喂牛羊;可以用来发酵,制造养料或燃料,也可直接燃烧。虽然也有采用秸秆制作成砖块,但制作成本高,操作难度大,都无法得到推广应用。
技术实现思路
本专利技术针对现有技术的不足,提出一种植物秸秆环保砖的制备方法,操作简便,成本低。为了实现上述专利技术目的,本专利技术提供以下技术方案:一种植物秸秆环保砖的制备方法,包括以下步骤:⑴、按重量比称取下述原料:水泥混凝土10-14、植物秸秆粉6-10、阻燃剂1-2、固化剂3-5;⑵、将水泥混凝土、植物秸秆粉、阻燃剂、固化剂混匀,置于砖模具中,静置2-5小时;隔绝空气加热至50-100℃,维持10-28min,冷却至常温。与现有技术相比,本专利技术具有以下优点:采用常规物料进行有效地组合,构成砖块的原料,经混匀、注模、静置、加热和冷却处理,即可得到砖坯;产品重量轻,强度合适,稳固性好;环保性能好,属于新型环保材质。具体实施方式下面结合实施例对本专利技术进行详细描述,本部分的描述仅是示范性和解释性,不应对本专利技术的保护范围有任何的限制作用。实施例1一种植物秸秆环保砖的制备方法,包括以下步骤:⑴、按重量比称取下述原料:水泥混凝土12、植物秸秆粉8、阻燃剂1.5、固化剂4;⑵、将水泥混凝土、植物秸秆粉、阻燃剂、固化剂混匀,置于砖模具中,静置4小时;隔绝空气加热 ...
【技术保护点】
一种植物秸秆环保砖的制备方法,包括以下步骤:⑴、按重量比称取下述原料:水泥混凝土10‑14、植物秸秆粉6‑10、阻燃剂1‑2、固化剂3‑5;⑵、将水泥混凝土、植物秸秆粉、阻燃剂、固化剂混匀,置于砖模具中,静置2‑5小时;隔绝空气加热至50‑100℃,维持10‑28min,冷却至常温。
【技术特征摘要】
1.一种植物秸秆环保砖的制备方法,包括以下步骤:⑴、按重量比称取下述原料:水泥混凝土10-14、植物秸秆粉6-10、阻燃剂1-2、固化剂3-5;...
【专利技术属性】
技术研发人员:梁文燊,
申请(专利权)人:广西北海浩邦新能源科技有限公司,
类型:发明
国别省市:广西,45