The invention discloses a method for processing xanthate adsorption in wastewater, including mesoporous silica spheres, the mesoporous silica 0.005g 0.05g containing 10 mg/L xanthate 60 mg/L 50 mL wastewater, pH adjusted to 3 with dilute hydrochloric acid 6, 10min 90 magnetic stirring at room temperature after min filtering. The invention adopts spherical mesoporous silica with high specific surface area, large pore volume and properties of ordered skeleton structure, and adjusting the pH to 3 6, the adsorption effect of xanthate wastewater significantly, can reach 97.56% removal rate of wastewater xanthate solution, the adsorption capacity reached 195.12 mg/ g, adsorption time is 15min compared with the existing, the adsorption time is about 60min, the adsorption efficiency is greatly improved.
【技术实现步骤摘要】
一种用于吸附废水中黄药的处理方法
本专利技术属于废水处理
，特别是用于吸附废水中黄药的处理方法。
技术介绍
黄药是硫化矿浮选中应用最广的捕收剂，橡胶工业中也常用其作硫化促进剂，也可用于分析化学和冶金工业，用途广泛，但黄药有刺激性臭味，中等毒性，工业废水中常因含有黄药而污染环境，需对废水中黄药进行处理，使其达到排放标准，以保护生态环境。废水中黄药的去除主要有生物降解法、化学沉淀法、氧化法、离子交换法、吸附法、酸化法等，化学沉淀、氧化法及酸化法处理成本过大，不经济，且易造成二次污染，后续处理步骤复杂。生物降解法处理技术优点多，但目前我国对生物法的研究仍处于实验室探索阶段，并未应用于工业生产中，且生物菌的生长不能准确控制，易造成新的环境问题。离子交换法处理量小，且循环周期长且成本高，不适用于连续处理大量的废水。采用吸附剂进行吸附具有有效、环保等特点，因此，在废水处理领域，高效的吸附剂备受青睐。目前对黄药的吸附主要有纳米材料、活性炭、蒙脱石及其改性物质等。中国专利申请（公布号为CN105018744B）中向湿法炼锌萃余液中加入三价铁盐使Fe3+浓度大于1g/L，然后...
【技术保护点】
一种用于吸附废水中黄药的处理方法，其特征在于：包括将0.005g‑0.05g的介孔二氧化硅加入含黄药10 mg/L‑60 mg/L的50 mL废水中，用稀盐酸调节pH至3‑6后，常温磁力搅拌10min‑90 min后过滤。
【技术特征摘要】
1.一种用于吸附废水中黄药的处理方法，其特征在于：包括将0.005g-0.05g的介孔二氧化硅加入含黄药10mg/L-60mg/L的50mL废水中，用稀盐酸调节pH至3-6后，常温磁力搅拌10min-90min后过滤。2.如权利要求1所述的一种用于吸附废水中黄药的处理方法，其特征在于：球状的介孔二氧化硅为自制的球状MC...
【专利技术属性】
技术研发人员：王杰，何文涛，秦舒浩，周颖，杨应娟，张覃，于杰，
申请(专利权)人：贵州省材料产业技术研究院，
类型：发明
国别省市：贵州,52
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。