The present invention relates to the technical field of anticorrosive adhesive tape, in particular to a tape, in accordance with the mass fraction meter comprises the following components: 15-30 parts of polyisobutylene rubber, acrylic rubber 45-60, adjacent benzene two formic acid two ester 8-15, polyethylene vinyl 70-90 copolymer, two methyl six generation zinc dithiocarbamate 20-34. Antioxidant 10-16, 5-13 diatomite, calcium carbonate 10-15, nanokaolin 4-9. Using the above formula, anticorrosive adhesive tape of the invention has good heat preservation effect, can to some extent improve the tape bonding effect; the invention has the advantages of simple structure, low cost, simple structure improvement is realized through the function of good anticorrosion.
【技术实现步骤摘要】
一种防腐胶带
本专利技术涉及防腐胶带
,特别是一种防腐胶带。
技术介绍
防腐蚀胶带制品主要有聚乙烯防腐胶带,聚丙烯纤维防腐胶带、聚乙烯660型防腐胶带,环氧煤沥青防腐冷缠带,其中聚乙烯防腐胶带和聚丙烯纤维防腐胶带在化工基建和管道弯头防腐中使用量比较大。而辐射交联聚乙烯热收缩缠绕带是防腐胶带的一种,经过辐射交联的聚乙烯有着更好的抗拉力,抗破坏力,由于他的胶层使用丁基型的热缩溶胶,使得剥离强度大大提高,一般在70N左右,是冷缠胶带3倍多,冷缠胶带在20N以上。防腐能力远远大于冷缠胶带,一般用于三层聚乙烯防腐结构的补口,补伤和异性管件的防腐。
技术实现思路
本专利技术需要解决的技术问题是提供一种防腐胶带。为解决上述的技术问题,本专利技术的一种防腐胶带,按照质量份数计包括以下组分:聚异丁烯橡胶15-30份,丙烯酸酯橡胶45-60份,邻苯二甲酸二辛酯8-15份,聚乙烯-醋酸乙烯共聚物70-90份,二甲基六代氨基甲酸锌20-34份,抗氧化剂10-16份,硅藻土5-13份,碳酸钙10-15份,纳米高岭土4-9份。进一步的,按照质量份数计包括以下组分:聚异丁烯橡胶15份,丙烯酸酯橡胶45份,邻苯二甲酸二辛酯8份,聚乙烯-醋酸乙烯共聚物70份,二甲基六代氨基甲酸锌20份,抗氧化剂10份,硅藻土5份,碳酸钙10份,纳米高岭土4份。进一步的,按照质量份数计包括以下组分:聚异丁烯橡胶30份,丙烯酸酯橡胶60份,邻苯二甲酸二辛酯15份,聚乙烯-醋酸乙烯共聚物90份,二甲基六代氨基甲酸锌34份,抗氧化剂16份,硅藻土13份,碳酸钙15份,纳米高岭土9份。进一步的,按照质量份数计包括 ...
【技术保护点】
一种防腐胶带,其特征在于,按照质量份数计包括以下组分:聚异丁烯橡胶15‑30份,丙烯酸酯橡胶45‑60份,邻苯二甲酸二辛酯8‑15份,聚乙烯‑醋酸乙烯共聚物70‑90份,二甲基六代氨基甲酸锌20‑34份,抗氧化剂10‑16份,硅藻土5‑13份,碳酸钙10‑15份,纳米高岭土4‑9份。
【技术特征摘要】
1.一种防腐胶带,其特征在于,按照质量份数计包括以下组分:聚异丁烯橡胶15-30份,丙烯酸酯橡胶45-60份,邻苯二甲酸二辛酯8-15份,聚乙烯-醋酸乙烯共聚物70-90份,二甲基六代氨基甲酸锌20-34份,抗氧化剂10-16份,硅藻土5-13份,碳酸钙10-15份,纳米高岭土4-9份。2.按照权利要求1所述的一种防腐胶带,其特征在于,按照质量份数计包括以下组分:聚异丁烯橡胶15份,丙烯酸酯橡胶45份,邻苯二甲酸二辛酯8份,聚乙烯-醋酸乙烯共聚物70份,二甲基六代氨基甲酸锌20份,抗氧化剂10份,硅藻土5份,碳酸钙10份,纳米高岭土4份。3.按照权利要求1所述的一种防腐胶带,其特征在于,按照质量份数计包括以下组分:聚异丁烯橡胶30份,丙烯酸酯橡胶60份...