The invention provides a lightweight wallboard mixing method added with diatomite. Raw materials: 15 sulphoaluminate cement 20, wheat shell powder 13 15 copies, 25 copies for calcium sulfate produced after flue gas desulfurization, diatomite 35, early strength water reducing agent 1 2. Wallboard manufacturing: mixing raw materials and mixing evenly, adding water to continue mixing, become concrete slurry, slurry through the molding machine or mold grouting and curing, forming a single wall panels or have hole cavity wallboard. The wall can adjust the indoor temperature and humidity, but also has the adsorption function, the construction of the wall of the building wall, can make the room to produce functional, on human health and comfort and good environmental protection and energy saving. It is suitable to be applied as lightweight wallboard batching method.
【技术实现步骤摘要】
添加有硅藻土的轻质墙板配料方法
本专利技术提供的是建材领域的墙板，具体地说是添加有硅藻土的轻质墙板配料方法。
技术介绍
墙板是用于隔墙的结构材料，通常用水泥或氧化镁水泥作胶结剂，并添加骨料或轻质材料，制成具有孔洞的墙体板，用于建筑物墙体的砌筑或隔断。但是这种墙板吸水性能差，不能产生呼吸和吸附作用，因此在调节房间的温湿度以及吸附灰尘和化学挥发物没有作用。
技术实现思路
为了使墙板能够具有调节温湿度和吸附性能，本专利技术提出了添加有硅藻土的轻质墙板配料方法。该方法通过在墙板原料中添加硅藻土，解决墙板性能提高的技术问题。本专利技术解决技术问题所采用的方案是：原料配料组成：硫铝酸盐水泥15-20份，小麦壳粉13-15份，用于烟气脱硫后产生的硫酸钙25份，硅藻土35份，减水早强剂1-2份。墙板制造：将原料混合搅拌均匀后，加水继续搅拌成为混凝土料浆，料浆经过成型机或模具注浆和固化，形成单体墙板或具有孔腔的墙板。积极效果，本专利技术墙板能够调节室内温湿度，而且具有吸附功能，采用该种墙板构筑建筑物的墙体后，能够使房间产生功能性，对人体健康和舒适度有益，并且环保节能。适宜作为轻质墙板应用。具体实施方式原料组成：硫铝酸盐水泥15-20份，小麦壳粉13-15份，用于烟气脱硫后产生的硫酸钙25份，硅藻土35份，减水早强剂1-2份。墙板制造：将原料混合搅拌均匀后，加水继续搅拌成为混凝土料浆，料浆经过成型机或模具注浆和固化，形成单体墙板或具有孔腔的墙板。所制成的墙板用于建筑物的隔墙砌筑或填充，作为墙体。技术原理：由于在所制备的混凝土料浆中加入了硅藻土，而硅藻土具有多孔性，能够吸附粉尘、空...
【技术保护点】
添加有硅藻土的轻质墙板配料方法，在原料中用硫铝酸盐水泥15‑20份，小麦壳粉13‑15份，减水早强剂1‑2份，将原料混合搅拌均匀后，加水继续搅拌成为混凝土料浆，料浆经过成型机或模具注浆和固化，形成单体墙板或具有孔腔的墙板；其特征是：在原料中还添加有用于烟气脱硫后产生的硫酸钙25份和硅藻土35份。
【技术特征摘要】
1.添加有硅藻土的轻质墙板配料方法，在原料中用硫铝酸盐水泥15-20份，小麦壳粉13-15份，减水早强剂1-2份，将原料混合搅拌均匀后，加水继续搅拌成...
【专利技术属性】
技术研发人员：刘来生，刘岩，
申请(专利权)人：辽宁中远高科有限公司，
类型：发明
国别省市：辽宁,21