The invention relates to an automobile production pipe surface cleaning agent comprises the following components by weight percentage: 8 to 22% turpentine oxidizing agent, thiourea 10 ~ 25%, 8 ~ 25% sodium lignosulfonate, sixteen alkyl two methyl benzyl ammonium chloride 10 ~ 20%, 6 ~ 15%, three sodium phosphate two ethylene glycol from 8 to 12%, three benzyl ether phosphonium bromide from 5 to 15%, the balance of deionized water. The range of products, oil stain and oil separation, good cleaning effect; cleaning automobile production pipe surface lubricants, metalworking fluids, grinding fluid and other dirt; cleaning ability and speed; repeated use, no pollution, and has anti rust capability. The cleaning liquid of the invention can quickly remove the dirt on the surface of the pipe of the automobile production, and can not corrode the automobile production pipe material.
【技术实现步骤摘要】
本专利技术涉及一种汽车生产管材表面清洗处理剂，属于汽车生产管材管清洗
技术介绍
在汽车生产管材管加工过程中，大量使用润滑油，润滑油具有良好的粘附性、润滑性，可以有效降低拉拔过程中的摩擦力，并保证汽车生产管材管表面的质量。加工好的汽车生产管材管主要用在热交换器、卫浴洁具上，尤其是核电用热交换器对于汽车生产管材管表面残留的炭膜等物质有着极高的要求，基于汽车生产管材管使用过程的性能要求，加工好的汽车生产管材管表面必须清洗干净，达到较高的清洁度。因此，必须对加工好的汽车生产管材管进行清洗，根据清洗工艺和清洁设备的情况，清洗剂必须满足以下要求去污能力强、挥发速度适中、挥发彻底；并且对金属无腐蚀作用。现有管材清洗剂多为溶剂型，如常用清洗剂的主要原料为煤油，煤油的清洗力和挥发速度均难以满足目前汽车生产管材管使用的需要。这些清洗剂存在的缺点是，清洗时间较长，清洗后的管材容易出现黑色表层，给后续加工带来麻烦，特别对精密元器件的加工造成影响，清洗剂对设备的腐蚀性也较强，增加设备成本，清洗效果不理想。
技术实现思路
本专利技术的目的在于提供一种汽车生产管材表面清洗处理剂，以便更...
【技术保护点】
一种汽车生产管材表面清洗处理剂，其特征在于由如下组分按质量百分比组成松节油8～22%、氧化剂硫脲10～25%、木质素磺酸钠8～25%、十六烷基二甲基苄基氯化铵10～20%、磷酸三钠6～15%、乙二醇丁醚8～12%、苄基三苯基溴化膦5～15%，余量为去离子水。
【技术特征摘要】
1.一种汽车生产管材表面清洗处理剂，其特征在于由如下组分按质量百分比组成松节油8～22%、氧化剂硫脲10～25%、木质素磺酸钠8～25%、十六烷基二甲基苄基氯化铵10～20%、磷酸三钠6～15%、乙二醇丁醚8～12%、苄基三苯基溴化膦5～15%，余量为去离子水。2.根据权利要求1所述的汽车生产管材表面清洗处理剂，其特征在于由如下组分按质量百分比组成松节油10～20%、氧化剂硫脲12～20%、木质素磺酸钠10～22%、十六烷基二甲基苄基氯化铵12～20%、磷酸三钠8～15%、乙...
【专利技术属性】
技术研发人员：何小荣，
申请(专利权)人：重庆伊曼环保设备有限公司，
类型：发明
国别省市：重庆;50