The invention discloses an easy two modified high reactive polydopamine coating modified calcium carbonate powder, the invention modified polydopamine film on the surface of calcium carbonate, the polydopamine films contain a large number of active functional groups, to provide more possibilities for further modification of calcium carbonate powder, powder modified then modified by titanate coupling agent, the modification effect is more excellent, calcium carbonate powder oil absorption value obtained, dispersion and surface affinity and so on were improved, the reaction activity and various system of higher products is more economical and efficient, wide use range.
【技术实现步骤摘要】
本专利技术涉及无机粉体表面改性
,尤其涉及一种易于二次修饰高反应活性的聚多巴胺包覆改性碳酸钙粉体及其制备方法。
技术介绍
碳酸钙是一种十分常见的无机粉末填料,其价格低廉、无毒无味、白度高、硬度好等优点,在橡胶制品、造纸、油墨、塑料、涂料等等领域均有广泛的应用,然而,碳酸钙本质上一种无机矿物质,与有机物质亲和相容性较差,直接填充将会导致产品性能严重劣化,使用范围严重受限,因此,在实际应用中需要对碳酸钙粉体进行改性处理。目前主要的改性方法有机械细化法、表面改性剂如偶联剂、脂肪酸及其盐、表面活性剂等改性两大类,两种方法各有其优势,改性后的碳酸钙性能也得到一定的改善。《硬脂酸-钛酸酯偶联剂改性重质碳酸钙粉体研究》一文以硬脂酸、钛酸酯偶联剂作为复合改性剂,无水乙醇作为分散剂,采用湿法球磨对粉体进行改性处理,取得了较为理想的改性效果,但是这种方法制备得到的产品为疏水性产品,在水性油墨、水性涂料领域应用受到限制,且附加功能不足,仅限于补强增韧用,需要做进一步的改性处理,以扩宽其使用范围。
技术实现思路
本专利技术目的就是为了弥补已有技术的缺陷,提供一种易于二次修饰高反应活性的聚多巴胺包覆改性碳酸钙粉体及其制备方法。本专利技术是通过以下技术方案实现的:一种易于二次修饰高反应活性的聚多巴胺包覆改性碳酸钙粉体,该改性碳酸钙粉体由以下重量份的原料制成:碳酸钙50、钛酸酯偶联剂2-3、无水乙醇60-80、盐酸多巴胺4-5、pH值为8-8.5的Tris-HCl缓冲液60-80。所述的一种易于二次修饰高反应活性的聚多巴胺包覆改性碳酸钙粉体的制备方法包括以下步骤:(1)先将盐酸多巴 ...
【技术保护点】
一种易于二次修饰高反应活性的聚多巴胺包覆改性碳酸钙粉体,其特征在于,该改性碳酸钙粉体由以下重量份的原料制成:碳酸钙50、钛酸酯偶联剂2‑3、无水乙醇60‑80、盐酸多巴胺4‑5、pH值为8‑8.5的Tris‑HCl缓冲液60‑80。
【技术特征摘要】
1.一种易于二次修饰高反应活性的聚多巴胺包覆改性碳酸钙粉体,其特征在于,该改性碳酸钙粉体由以下重量份的原料制成:碳酸钙50、钛酸酯偶联剂2-3、无水乙醇60-80、盐酸多巴胺4-5、pH值为8-8.5的Tris-HCl缓冲液60-80。2.如权利要求1所述的一种易于二次修饰高反应活性的聚多巴胺包覆改性碳酸钙粉体的制备方法,其特征在于,其制备方法包...
【专利技术属性】
技术研发人员:陈永忠,
申请(专利权)人:青阳县永诚钙业有限责任公司,
类型:发明
国别省市:安徽;34