The invention relates to a porous polyvinyl alcohol material and a preparation method thereof, which belongs to the technical field of polyvinyl alcohol materials. The hole of polyvinyl alcohol material comprises the following raw materials by weight: 80 polyvinyl alcohol 90, hydrochloric acid 5 8 copies, 25 copies, 20 - NaCl 10 20 copies, 20 copies of 10 isopropyl alcohol and deionized water 800 850. The present invention porgenic agent in PVA solution (inorganic salts, alcohols, etc.) with hydrochloric acid or sulfuric acid as the catalyst for the acetalization, with aldehyde acetal material, in the premise of control polyvinyl alcohol PVA mixed solution viscosity, prepared a water-insoluble PVA foam material.
【技术实现步骤摘要】
本专利技术涉及一种聚乙烯醇材料及其制备方法，更具体地说，本专利技术涉及一种孔性聚乙烯醇材料及其制备方法，属于聚乙烯醇材料
技术介绍
泡孔材料因其具有较低的比重，较佳的物理综合性能而在各个方面获得了广泛的应用。除已经广泛应用的聚氨酯泡沫、聚苯乙烯泡沫外，聚乙烯醇缩丁醛泡孔材料也正受到人们的关注。聚乙烯醇缩甲醛泡孔材料为白色开孔结构，干态质地较硬，有较高的机械强度，湿态质地柔软富有弹性。由于微孔相互贯通，并且有亲水性，耐有机溶剂、药品、耐油、耐老化、耐磨、耐干热和生物相容性好等特点，用途十分广泛。该泡孔材料除可用作空气压缩机、各种引擎吸气、室内空气净化和各种油类、有机溶剂、水和涂料滤材外，还可作为汽车、浴池、厨房、印刷洗涤用具，油鞣革代用品和玻璃等的抛光材料。作为具有较佳生物相容性的材料，也可作填塞胸腔术后的残腔和在整形外科方面填塞面部因伤病致缺损凹陷等医用材料。现有技术缺乏一种不溶于水的聚乙烯醇材料。
技术实现思路
本专利技术旨在解决现有技术中缺乏不溶于水的聚乙烯醇材料的问题，提供一种孔性聚乙烯醇材料，该孔性聚乙烯醇材料不溶于水。为了实现上述专利技术目的，其...
【技术保护点】
一种孔性聚乙烯醇材料，其特征在于：包括以下按照重量份数计的原料：聚乙烯醇 80‑90份盐酸 5‑8份丁醛 20‑25份NaCl 10‑20份异丙醇 10‑20份去离子水 800‑850份。
【技术特征摘要】
1.一种孔性聚乙烯醇材料，其特征在于：包括以下按照重量份数计的原料：聚乙烯醇80-90份盐酸5-8份丁醛20-25份NaCl10-20份异丙醇10-20份去离子水800-850份。2.根据权利要求1所述的一种孔性聚乙烯醇材料的制备方法，其特征在于：包括以下工艺步骤：A、按配方要求准确称取聚乙烯醇、去离子水、盐酸、异丙醇和NaCl于一模具容器内...