The invention discloses a titanium dioxide, Polyethylene double coated calcium carbonate filler and preparation method thereof, which is characterized in that is made of the following raw materials in weight portion: 40 calcium oxide 50, CO2 amount of acetyl acetone 5 10 sodium stearate 6 12, 15 25 butyl titanate, poly ethylene resin 25 35, two methyl silicone oil 8 12, 200 250 deionized water. The invention uses titanium dioxide and polyethylene resin double coated on calcium carbonate powder, calcium carbonate powder not only enhances the acid resistance, whiteness and fireproof performance, while improving the organic substrate and fusion, which can meet the requirements of the more widely used.
【技术实现步骤摘要】
本专利技术涉及一种复合改性碳酸钙粉体及其制备，尤其涉及一种二氧化钛、聚乙烯双重包覆碳酸钙无机填料及其制备方法。
技术介绍
粉体的表面改性处理就是根据粉体材料应用的需要，利用物理、化学、机械等方法有目的地改变粉体材料表面的物理化学性质，如表面组成、结构和官能团、表面能、表面润湿性、电性、光性、吸附和反应特性等等，以满足现代材料和新技术发展的需要。在塑料、人造大理石等高分子材料工业及高聚物基复合材料应用领域中，碳酸钙粉体填料占有很重要的地位。碳酸钙填料不仅可以减低材料的生产成本，还能提高材料的硬度、刚性或尺寸稳定性，改善材料的力学性能并赋予材料某些特殊的物理化学性能，如耐腐蚀性、耐候性、阻燃性和绝缘性等。但由于碳酸钙填料与基质，即有机高聚物的表面或界面性质不同，相容性较差，因而,难以在基质中均匀分散，直接或过多地填充往往容易导致材料的某些力学性能下降以及易脆化等缺点。因此，除了对碳酸钙填料的粒度和粒度分布的要求之外，还必须对其表面进行改性，以改善其表面的物理化学特性，增强其与有机聚合物或树脂等基体的相容性和在有机基体中的分散性，以提高材料的机械性能及综合性能。段好在其硕士学位论文《超细碳酸钙粉体的干法表面改性研究》中，利用油酸-马来酸酐复合改性剂对碳酸钙粉体进行改性，但是当碳酸钙作为塑料、涂料等填料时，还存在着耐酸度不佳，与有机基底的融合性欠缺等缺点。
技术实现思路
基于以上的思考，本专利技术旨在提供一种复合改性碳酸钙无机填料及其制备方法，用以解决当碳酸钙作为塑料、涂料等填料时，存在的耐酸度不佳，与有机基底的融合性欠缺等缺点。本专利技术所要解决的技术问题采用以下...
【技术保护点】
一种二氧化钛、聚乙烯双重包覆碳酸钙无机填料，其特征在于，由以下重量份的原料制成：氧化钙40‑50， CO2适量，乙酰丙酮5‑10，硬脂酸钠6‑12，钛酸丁酯15‑25，聚乙烯树脂25‑35，二甲基硅油8‑12，去离子水200‑250。
【技术特征摘要】
1.一种二氧化钛、聚乙烯双重包覆碳酸钙无机填料，其特征在于，由以下重量份的原料制成：氧化钙40-50，CO2适量，乙酰丙酮5-10，硬脂酸钠6-12，钛酸丁酯15-25，聚乙烯树脂25-35，二甲基硅油8-12，去离子水200-250。2.根据权利要求1所述的一种二氧化钛、聚乙烯双重包覆碳酸钙无机填料及其制备方法，其特征在于，由以下步骤制成：a.将氧化钙固体粉碎成粉末状，加入去离子水，60-100℃下搅拌反应2-3h，反应后的浆液陈化1-3h后，将浆液转入到碳化反应釜中，CO2和空气通过转子流量计计量后混合，通入碳化反应釜底部的气体分布器；当pH＜7时，结束反应，得碳酸钙浆液；b.70-90℃下，向步骤a所得碳酸钙...
【专利技术属性】
技术研发人员：王文杰，
申请(专利权)人：青阳县金山粉业有限公司，
类型：发明
国别省市：安徽;34