The invention discloses a low lead brass alloy and a preparation method thereof, wherein, brass alloy by weight, which is composed of: Cu: 55~60, Zn: 30~35, Pb: 0.05~0.25, 0.5~1.0, molybdenum and bismuth:: 0.1~0.5, 0.1~1.0, P: Al: 0.01~0.05, tin a: 0.1~0.7, Fe: 0.1~0.5; preparation method is through the process of preheating, melting and casting components of molding and mold, low lead brass alloy. Low lead brass alloy prepared by the invention has excellent ductility and excellent machining performance and excellent corrosion resistance, and has the function of sterilization for water supply system of pipeline equipment, bathroom hardware at.
【技术实现步骤摘要】
本专利技术涉及黄铜合金领域，具体涉及一种低铅黄铜合金及其制备方法。
技术介绍
黄铜是由铜和锌所组成的合金，如果只是由铜、锌组成的黄铜就叫作普通黄铜；如果是由二种以上的元素组成的多种合金就称为特殊黄铜，如由铅、锡、锰、镍、铅、铁、硅组成的铜合金。黄铜有较强的耐磨性能，特殊黄铜又叫特种黄铜，它强度高、硬度大、耐化学腐蚀性强，还有切削加工的机械性能也较突出。由黄铜所拉成的无缝铜管，质软、耐磨性能强。黄铜无缝管可用于热交换器和冷凝器、低温管路、海底运输管。制造板料、条材、棒材、管材，铸造零件等。含铜在62%～68%，塑性强，制造耐压设备等。为了改善黄铜性质，熟知黄铜是含铅，质量百分数多为1%～3%，以达到产业所需的机械特性铅作为一种对人体及环境危害极大的元素，比如铅对人体血液及神经系统，特别是对儿童的肾和脑神经可造成不可逆转的损伤。近年来，世界各国对铅给人体及环境带来的危害的认识越来越深入，并达成了广泛的共识，政府、各种组织针对铅的危害控制也形成了各种限令。比如：欧盟《电气电子设备有害物质之禁用令》2003年1月正式颁布，2006年7月1日正式实施，中国亦随后颁布了《电子信息产品污染控制管理办法》并于2007年3月1日起实施，近来又新颁布了水龙头国家环保标准《环境标志产品技术要求水嘴》，并从2008年4月1日开始正式实行。这一系列环保举措，都对金属中重金属元素铅的含量或析出量予以了严格限制。鉴于以上原因，开发加工用无铅铜合金材料，既符合环保发展趋势，又具有良好的市场前景。
技术实现思路
本专利技术的目的在于克服现有技术...
【技术保护点】
一种低铅黄铜合金，其特征在于按重量份比，其组成为：铜：55~60份，锌：30~35份，铅：0.05~0.25份，铋：0.5~1.0份，钼：0.1~0.5份，铝：0.1~1.0份，磷：0.01~0.05份，锡：0.1~0.7份，铁：0.1~0.5份。
【技术特征摘要】
1.一种低铅黄铜合金，其特征在于按重量份比，其组成为：铜：55~60份，锌：30~35份，铅：0.05~0.25份，铋：0.5~1.0份，钼：0.1~0.5份，铝：0.1~1.0份，磷：0.01~0.05份，锡：0.1~0.7份，铁：0.1~0.5份。
2.根据权利要求1所述的低铅黄铜合金，其特征在于按重量份比，其组成为：铜：56份，锌：32份，铅：0.12份，铋：0.6份，钼：0.3份，铝：0.3份，磷：0.04份，锡：0.5份，铁：0.4份。
3.权利要求1或2所述的低铅黄铜合金的制备方法，其特征在于包括如下步骤：
(1)将所述各组分按重量份混合预热至400℃~500℃...
【专利技术属性】
技术研发人员：刘莉，王爽，邱晶，刘晓东，黄明明，
申请(专利权)人：苏州莱特复合材料有限公司，
类型：发明
国别省市：江苏;32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。