一种三次风管用纳米碳化钽高温陶瓷闸阀板制造技术

本发明专利技术公开了一种三次风管用高温陶瓷闸阀板：该高温陶瓷闸阀板具有寿命长、耐磨、耐腐蚀、耐压强度高、易安装等优点。由陶瓷块和耐热钢构成，陶瓷块包括原始料为刚玉、碳化硅和金属硅，外加纳米碳化钽复合物、添加剂和水，经热压成型，中间有一个直径6cm充满的焊孔的长条状，脱模干燥后，放入干燥器烘干，即可得到陶瓷块。

A three nanometer tantalum carbide ceramic tube wind valve plate

The invention discloses a high temperature ceramic gate valve plate for the three air pipe, which has the advantages of long service life, wear resistance, corrosion resistance, high pressure resistance, easy installation, etc.. Composed of ceramic block and heat resistant steel, ceramic blocks including raw material for corundum, silicon carbide and silicon metal, nanometer tantalum carbide composite material, additive and water, the hot forming, welding holes with a diameter of 6cm is in the middle of a long strip, demoulding after drying, into the dryer drying, can obtain the ceramic block.

【技术实现步骤摘要】

本专利技术涉及了大型水泥窑三次风管用高温陶瓷闸阀，特别涉及一种主要成分包括碳化硅、二钼化硅的碳化硅陶瓷衬管。
技术介绍
在新型干法水泥窑中主要是通过调节三次风阀米调节回转窑内的风量并确保分解炉内的煤粉能充分燃烧，风阀的调节对回转窑烧成工艺的调节起着至关重要的作用。三次风阀在使用中始终受到高速气流的正面冲击，烟气流速高(高达30m/s)，烟气中飞砂浓度大，颗粒硬度高，所以该部位磨损相当严重。传统的三次风阀为耐热钢加上浇注料，然而采用浇注料施工，无法保证材料的耐磨性能，损坏较快，平均使用寿命只能用3-4个月左右，严重影响了水泥窑烧成工艺的调节。生产现场三次风阀损害的具体形式主要有：风阀的浇注料磨损；风阀骨架变形卡死；浇注料大块剥落；浇注料材质的爆裂等。
技术实现思路
本专利技术要解决的上述技术问题是提供了一种有以下特点的大型水泥窑三次风管用高温陶瓷闸阀板：该高温陶瓷闸阀板具有寿命长、耐磨、耐腐蚀、耐压强度高、易安装等优点。本专利技术的大型水泥窑喷煤管用高温陶瓷闸阀本文档来自技高网...

【技术保护点】
一种三次风管用纳米碳化钽高温陶瓷闸阀板，其特征在于：本专利技术原始料的配比为：刚玉加入量占原始料总重量的百分比为65‑80％，碳化硅加入量占原始料总重量的百分比为10‑30％，金属硅加入量占原始料总重量的百分比为5‑10％，纳米碳化钽复合物加入量占原始料总重量的百分比为0.1‑1％，添加剂加入量占原始料总重量的百分比为2‑8％。

【技术特征摘要】
1.一种三次风管用纳米碳化钽高温陶瓷闸阀板，其特征在于：本发明原始料的
配比为：刚玉加入量占原始料总重量的百分比为65-80％，碳化硅加入量占原始
料总重量的百分比为10-30％，金属硅加入量占原始料总重量的百分比为5-10％，
纳米碳化钽复合物加入量占原始料总重量的百分比为0.1-1％，添加剂加入量占
原始料总重量的百分比为2-8％。
2.根据权利要求1所述的一种三次风管用纳米碳化钽高温陶瓷闸...