The invention discloses a rolling slurry powder processing method, the method includes mixing the powder by sieving, adding carrier, rolling silver paste, which is characterized in that the sieve processing in 150 ~ 200 mesh screen mesh, wherein the carrier is: ethyl cellulose was 11.4%, Ding Jika will be alcohol 81.8%, three citric acid ester 6.6%, 0.2% edible blend oil. The present invention of silver powder, add other granular materials in the screened processing, adding carrier, rolling process of silver, silver powder, the particle size distribution in rolling slurry before optimization, to avoid abnormal silver powder into the silver paste, the silver powder dispersion, organic carrier can the infiltration of silver, so that the silver paste consistency, uniformity and stability further improve.
【技术实现步骤摘要】
本专利技术涉及一种轧浆前粉体处理方法,属于电阻器原件等基础材料的
技术介绍
随着电子信息产业的迅速发展,带动了电子银浆和银粉行业的发展。银的导电性和导热性使其成为电子工业不可缺少的材料,银粉及其电子银浆系列产品是电子工业中应用最为广泛和用量最大的一种贵金属电子材料,是生产各种电子元器件产品的基本和关键功能材料。银粉在化学还原过程中很难避免产生较大颗粒的粉体;同时其它添加物粉体在磨制过程中也无法做到单一的粒径分布,总会存在一些分布异常的颗粒。现有技术轧浆的步骤是:称量好各种颗粒物料,人工用勺子搅拌均匀,加入载体,轧制银浆。本步骤也可以用动力混合机将称量好的各种颗粒物料搅拌2~4h,再加入载体,轧制银浆。如:2011.12.21,中国专利技术专利公开号CN102290118A,公开了一种电子银浆及其制备工艺,将玻璃粉,银粉,有机载体和添加剂在搅拌机里混合均匀,再在三辊机上反复滚扎,由于,银粉和其它各种颗粒物料未进行轧浆前处理,就直接进行人工搅拌或动力混合机搅拌,轧制的银浆的一致性、均匀性、稳定性较差,亮片也多。
技术实现思路
本专利技术针对现有技术的不足,目的是提供一种轧浆前粉体处理方法,为了解决上述技术问题,本专利技术是通过以下技术方案实现的:一种轧浆前粉体处理方法,该方法包括将混合粉体进行过筛处理,加入载体,轧制银浆,其特征在于,所述过筛处理中筛网目数为150~200目,所述载体为:乙基纤维素为11.4%,丁基卡必醇为81.8%,柠檬酸三丁酯为6.6%,食用调和油为0.2%。与现有技术相比,本专利技术通过对银粉、其它添加的颗粒物料进行过筛的处理,加 ...
【技术保护点】
一种轧浆前粉体处理方法,该方法包括将混合粉体进行过筛处理,加入载体,轧制银浆,其特征在于,所述过筛处理中筛网目数为150~200目,所述载体为:乙基纤维素为11.4%,丁基卡必醇为81.8%,柠檬酸三丁酯为6.6%,食用调和油为0.2%。
【技术特征摘要】
1.一种轧浆前粉体处理方法,该方法包括将混合粉体进行过筛处理,加入载体,轧制银浆,其特征在于,所述过筛处理中筛网目数为1...