The invention discloses a chromium iron alloy and its preparation process comprises the following components in weight percentage: 0.09-0.15% carbon, 26-32% chromium, silicon, titanium and nickel 0.10-0.15% 0.12-0.20% 0.22-0.32%, 0.18-0.25%, 0.10-0.30%, copper, manganese, phosphorus, sulfur tin 0.38-0.45% 0.03-0.05% 0.01-0.03% and unavoidable impurities is less than 0.06% and the allowance for iron. Compared with the prior art, the preparation process of the invention can effectively improve the performance of process parameters of ferrochrome, ferrochrome processing and heat treatment to improve the strength, effectively ensuring the casting performance, mechanical properties, and chromium alloy strength, toughness, ductility and wear resistance are improved effectively.
【技术实现步骤摘要】
本专利技术涉及铬铁合金
，具体涉及一种铬铁合金及其制备工艺。
技术介绍
铬铁合金可作炼钢添加料生产多种特种钢，如不锈钢、弹簧钢、工具钢等，这些特种钢和特种合金在航空、宇航、汽车、造船以及国防工业领域得到广泛的应用。同时，金属铬也属于国家战略金属，主要用于与钴、镍、钨等元素冶炼特种合金。然而，我国铬矿资源贫乏，保有储量仅占世界储量的0.15％，95％铬铁矿依靠进口，同时现有生产工艺中铬铁矿粉矿也无法得到有效地利用，因此开发出一条合理利用铬铁矿冶炼铬铁合金的工艺尤为重要。
技术实现思路
本专利技术旨在提供了一种铬铁合金及其制备工艺。本专利技术提供如下技术方案：一种铬铁合金及其制备工艺，由以下重量百分比的组分组成：碳0.09-0.15％、铬26-32％、硅0.12-0.20％、钛0.22-0.32％、镍0.10-0.15％、锰0.18-0.25％、铜0.10-0.30％、锡0.38-0.45％、硫0.03-0.05％、磷0.01-0.03％、不可避免杂质小于0.06％、余量为铁。一种铬铁合金及其制备工艺，包括以下步骤：(1)将铬矿粉和铁矿粉进行混合，得到混合物料；(2)将所述的混合物料先在电熔炉中用石墨坩埚溽热至650-700℃，熔化成铬铁合金液，再依次向铬铁合金液中加入硅、钛、镍、锰、铜、锡熔化，随后温度降至580-620℃，均匀搅拌3-5分钟；(3)在氩气的保护下，将还原剂、助还原剂和粘结剂加入上述铬铁合金液中，熔化完全后，搅拌4-6分钟；(4)除去浮渣，在6...
【技术保护点】
一种铬铁合金及其制备工艺，其特征在于,由以下重量百分比的组分组成：碳0.09‑0.15％、铬26‑32％、硅0.12‑0.20％、钛0.22‑0.32％、镍0.10‑0.15％、锰0.18‑0.25％、铜0.10‑0.30％、锡0.38‑0.45％、硫0.03‑0.05％、磷0.01‑0.03％、不可避免杂质小于0.06％、余量为铁。
【技术特征摘要】
1.一种铬铁合金及其制备工艺，其特征在于,由以下重量百分比
的组分组成：碳0.09-0.15％、铬26-32％、硅0.12-0.20％、钛
0.22-0.32％、镍0.10-0.15％、锰0.18-0.25％、铜0.10-0.30％、锡
0.38-0.45％、硫0.03-0.05％、磷0.01-0.03％、不可避免杂质小于
0.06％、余量为铁。
2.根据权利要求1所述的一种铬铁合金及其制备工艺，其特征
在于，包括以下步骤：
(1)将铬矿粉和铁矿粉进行混合，得到混合物料；
(2)将所述的混合物料先在电熔炉中用石墨坩埚溽热至650-700
℃，熔化成铬铁...
【专利技术属性】
技术研发人员：梅百荣，
申请(专利权)人：铜陵安东铸钢有限责任公司，
类型：发明
国别省市：安徽;34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。