人造花岗石、大理石机械配件及其制备方法技术

本发明专利技术公开了一种人造花岗石、大理石机械配件及其制备方法，属于机械配件加工领域。人造花岗石、大理石机械配件，由重量百分比为８０％－９３％的骨料和２０％－７％的胶料，经配料、装模、密实等工艺制成。其中，骨料是粒度为０．０１－２５ｍｍ的天然花岗石颗粒或大理石颗粒。与现有技术相比，本发明专利技术的人造花岗石、大理石机械配件具有较强的振动阻尼和较低的成本，广泛应用于机床设备、检测设备、计量仪器的配件之中，具有很好的推广应用价值。

Artificial granite, marble machinery fittings and preparation method thereof

The invention discloses an artificial granite, a marble mechanical component and a preparation method thereof, belonging to the processing field of mechanical fittings. Made of artificial granite and marble mechanical fittings, the aggregate is made up of 80% to 93% weight percentage and 20% - 7% glue material, which is made by batching, molding and compacting. The particle size of aggregate is natural granite or marble particles of the 0.0125mm particles. Compared with the prior art, the invention of artificial granite, marble mechanical fitting has strong vibration damping and low cost, is widely used in machine tools, testing equipment, measuring instrument and accessories, has the very good application value.

【技术实现步骤摘要】

本专利技术涉及一种非金属机械配件，具体地说是一种。
技术介绍
现有技术中，各种加工机床、检测设备大多是以铸铁、钢材等金属材料加工而成的。随着对机械配件加工精度要求的提高，加工母机的运转速度也大为提高，这样，加工过程中就会产生剧烈的震动。但是，金属材料却因为自身削减震动的能力不强，无法有效地吸收掉母机运转过程中产生的震动，加上金属材料的热膨胀系数大，使得设备的安装调试过程变得十分复杂，并且配件的加工精度也因此受到极大限制。另外，金属机械配件的加工过程还存在能源消耗量大、污染环境等不足。目前，虽然有许多种技术可以生产人造花岗石或人造大理石材料，但却因强度、硬度等物理指标无法达到机械配件的性能要求，而只能充当装饰材料。
技术实现思路
本专利技术的技术任务是针对上述现有技术的不足，提供一种人造花岗石、大理石机械配件，该机械配件为非金属合成材料制成，在满足金属配件各项性能指标的同时，增加了配件的振动阻尼及耐热性，且生产成本大大较低。本专利技术的另一个技术任务是提供该人造花岗石、大理石机构配件的制备方法。本专利技术的技术任务是按以下方式实现的人造花岗石、大理石机械配件，由以下重量百分比的原料制成本文档来自技高网...

【技术保护点】
人造花岗石、大理石机械配件，其特征在于它由以下重量百分比的原料制成：　　　　骨料８０－９３％　　胶料２０％－７％；　　　　所述骨料是粒度为０．０１－２５ｍｍ的天然花岗石颗粒或大理石颗粒。