一种清洁的轻质蜂窝陶瓷抗热震炉头及其制造方法技术

本发明专利技术公开了一种清洁的轻质蜂窝陶瓷抗热震炉头，它包含以下重量份的原料制备而成：堇青石４０～９５，熔融石英５～６０，润滑剂１～１０，造孔剂５～２５，堇青石的细度为２５０目筛余１～７％，堇青石与熔融石英二者之和为１００。本发明专利技术还公开了这种炉头的制造方法。这种炉头加工成本低，热稳定性好，抗热震能力强，烧成范围宽，可在较低温度下烧成，能保证成品尺寸稳定外观规整。成品不仅质轻、吸水率高，而且显气孔率高，使用时吸热少，吸附面积大，辐射面积大，节能效果好，有利于保护环境。

Clean lightweight honeycomb ceramic thermal shock proof furnace head and manufacturing method thereof

The invention discloses a clean and lightweight honeycomb ceramic thermal shock furnace head, which comprises the following parts by weight of the prepared cordierite: 40 ~ 95, 5 ~ 60 fused silica, lubricants 1 ~ 10, 5 ~ 25 pore forming agent, cordierite fineness of 250 mesh screen more than 1 ~ 7% cordierite and fused quartz, two and 100. The invention also discloses the manufacturing method of the furnace head. The utility model has the advantages of low processing cost, good thermal stability, strong thermal shock resistance, wide firing range, burning at lower temperature, stable size of the finished product and orderly appearance. The finished product has the advantages of light weight, high water absorption rate, high porosity, low heat absorption when used, large adsorption area, large radiation area, good energy saving effect, and favorable environment protection.

【技术实现步骤摘要】

本专利技术属于陶瓷，尤其涉及一种轻质蜂窝陶瓷抗热震炉头，本专利技术还涉及这种炉头的制造方法。
技术介绍
陶瓷炉头用于液化气、天然气、煤气等气体燃料炉的炉面，以充分混合燃气、提高燃烧温度、净化燃烧产物、产生辐射功能。目前我国多以重质材料生产，以细密的机械孔实现上述目的，称蜂窝陶瓷灶片。近年新出现了一种轻质材料，吸水率在30～46％之间，多以煤炭作造孔剂，微孔中往往有煤渣残留。目前西班牙等国生产有这种清洁的轻质、多孔、抗热震蜂窝陶瓷，其主要成份为堇青石、原顽辉石、方石英、莫来石等。为了降低烧成温度，在生产中常用微粉配料，微粉细度需在500目以上，加工成本较高，而且陶瓷成品中含有10～15％的方石英，800℃的膨胀系数为6.02×10-6/℃，热稳定性很差，如Φ173×12.7炉头1100℃到冷水中一次开裂。国内目前也已开始生产这种轻质、多孔蜂窝陶瓷，生产中多以热压铸方法成型，需要排蜡，所用吸附剂又常常粘附在制品孔中及表面，影响火焰通过及外观效果。
技术实现思路
本专利技术的目的是提供一种表面清洁、膨胀系数较小、烧成温度易于控制、生产成本低的轻质蜂窝陶瓷炉头，本专利技术还提供这种炉头的制造本文档来自技高网...

【技术保护点】
一种清洁的轻质蜂窝陶瓷抗热震炉头，其特征在于它包含以下重量份的原料制备而成：堇青石４０～９５，熔融石英５～６０，润滑剂１～１０，造孔剂５～２５，堇青石的细度为２５０目筛余１～７％，堇青石与熔融石英二者之和为１００。

【技术特征摘要】

【专利技术属性】
技术研发人员：刘金炳，陈建庭，
申请(专利权)人：陈建庭，刘金炳，
类型：发明
国别省市：41[中国|河南]