非烧结粘土砖的配方组成比例

本发明专利技术属于一种非烧结粘土建筑材料的配方，特别涉及一种非烧结粘土砖的配方。一种非烧结粘土砖的配方，其特殊之处在于：含有粘土（干基）８０～８５％（重量）复合活性外加剂０．１－０．６％（重量）、水泥３－１０％（重量）以及平衡量水所组成，复合活性外加剂主要含有二氧化硅１２－１７％（重量）、三氧化硫３０－５０％（重量）、氧化钠５－１０％（重量）、三氧化二铝５－１０％（重量）、低分子树脂１０－１５％（重量）以及平衡水所组成。本发明专利技术所提供的非烧浇结粘土的配方，制成的非浇结粘土砖质量符合普通浇结砖ＧＢ５１０１～８１的要求，成本均低于浇结砖和蒸养纸址砖，具有能耗低，不污染环境的优点。

Formulation of non sintered clay brick

The invention belongs to a formulation of a non sintered clay building material, in particular to a formula for a non sintered clay brick. A non sintered clay brick formula, which is characterized by containing clay (dry basis) 80 ~ 85% (weight) composite activity admixture 0.1 - 0.6% (weight), cement 3 - 10% (weight) composition and balance the amount of water, mainly containing silica composite active admixture 12 - 17% (weight), three so 30 - 50% (weight), sodium 5 - 10% (weight), three 5 - 10% two aluminum oxide (low molecular weight), 10 - 15% (weight) resin composition and water balance. The formula of burning clay sintering provided by the invention is made of non sintering clay brick quality conforms to the common cast brick GB5101 ~ 81 requirements, cost is lower than that of cast sintering bricks and autoclaved brick paper site, with low energy consumption, no environmental pollution.

【技术实现步骤摘要】

本专利技术属于一种非烧结粘土建筑材料的配方，特别涉及一种非烧结粘土砖的配方。
技术介绍
众所周知。自古以来建筑上使用的红址砖，一般以粘土为材料，用燃料烧结而成，其弊端是能耗大、毁坏良田、污染环境和破坏生态平衡。而非烧结粘土砖一般分为两类，一类用红址土、石灰等混合压制成型，经蒸养和养护而成，但工艺复杂、能耗大、污染环境，不利推广；另一类是用粘土、水泥、外加剂等混合压制成型，自然养护而成，但由于外加剂单一，活性差，因而水泥用量一般在10％以上，生产成本过高，难于实施。
技术实现思路
本发是为了弥补现有技术的不足，提供了一种复合活性外加剂，从而使得大大降低非烧结粘土砖的水泥用量，制备一种能耗低、不污染环境、生产成本低的非烧结粘土砖。本专利技术是通过如下技术方案实现的一种非烧结粘土砖的配方，其特殊之处在于含有粘土(干基)80～85％(重量)复合活性外加剂0.1-0.6％(重量)、水泥3-10％(重量)以及平衡量水所组成，复合活性外加剂主要含有二氧化硅12-17％(重量)、三氧化硫30-50％(重量)、氧化钠5-10％(重量)三氧化二铝5-10％(重量)、低分子树脂10-15％(重量)以及平衡水本文档来自技高网...

【技术保护点】
一种非烧结粘土砖的配方，其特征是：含有（重量％）粘土（干基）８０～８５复合活性外加剂０．１～０．６水泥３～１０以及平衡量水所组成，复合活性外加剂主要含有（重量％）二氧化硅１２～１７ 三氧化硫３０～５０％氧化钠５－１０三氧化二铝５－１０低分子树脂１０－１５以及平衡水所组成。

【技术特征摘要】

【专利技术属性】
技术研发人员：张玉凤，
申请(专利权)人：张玉凤，
类型：发明
国别省市：88[中国|济南]