一种氧化锆注塑成型方法技术

一种氧化锆注塑成型方法及粉料有机载体，采用一种氧化锆陶瓷的注射成型方法和粉料有机载体及合理的脱脂工艺：以氧化锆粉末为主体，加入一定分量的经优化组合的有机载体，采用注射成型工艺制作坯体，通过合理的脱脂、烧结工艺制成高性能的氧化锆陶瓷制品。所述的粉料有机载体包括：聚乙烯、聚丙烯、植物油、油酸、石蜡。所述的氧化锆粉料与粉料有机载体的配比为１００∶１０－８０重量份数。所述的粉料有机载体的选用配比为粉料有机载体总重量的聚乙烯１０－３０％，聚丙烯１０－３０％，植物油５－４０％，油酸１－５％，石蜡５－５０％，粉料有机载体可在所选范围内任意组配。

Process for injection molding of zirconium oxide

And a zirconia powder injection molding method of organic material carrier, using the injection molding method and a powder of zirconia ceramic material of organic carrier and reasonable degreasing process with zirconia powder as the main component of the organic carrier by adding some optimized combination, making the body by injection molding, zirconia ceramic products high performance made by reasonable debinding and sintering process. The powder organic carrier comprises polyethylene, polypropylene, vegetable oil, oleic acid and paraffin wax. The ratio of the zirconia powder and the powder organic carrier is 100 to 10-80 weight parts. The powder used as carrier for powder ratio of organic and organic carrier of the total weight of polyethylene 10 - 30%, PP 10 - 30%, 5 - 40% vegetable oil, oleic acid 1 - 5%, 5 - 50% paraffin wax powder, organic carrier can be selected in the range of arbitrary assembly.

【技术实现步骤摘要】

本专利技术涉及一种结构陶瓷的制作方法及粉料有机载体和合理的脱脂工艺，尤其是指一种高性能氧化锆陶瓷制品的注射成型制作方法及粉料有机载体和合理的脱脂工艺，属于结构陶瓷加工制作领域，主要用于加工制作氧化锆结构陶瓷制品。
技术介绍
氧化锆陶瓷具有高硬度、高韧性、高密度、机械性能优异等传统陶瓷无以伦比的优点，是二十一世纪最有前途，最具经济效益的结构陶瓷材料之一。氧化锆结构陶瓷广泛地用于航天、通讯、机械、化工等诸多行业。氧化锆是一种多变晶体材料，如果不采取稳定或部分稳定晶体相转变的原料制备工艺，就会使陶瓷制品在烧成过程中因晶相转变的体积膨胀或收缩产生裂纹，从而无法制造出高强度、高硬度、高韧性的氧化锆陶瓷制品。目前，国内已有多家高等院校、研究所成功研制开发出亚微米级部分稳定氧化锆(PSZ)粉末。形成亚微米氧化锆粉体产业化的企业已有数家。从而在材质上确保了氧化锆结构陶瓷的优质性能。通过材料科学家的反复研究试验，为了提高氧化锆陶瓷的性能，采用一种陶瓷注射成型技术。陶瓷注射成型工艺能制造出形状复杂的高精密度陶瓷零部件，且易于规模化和自动化生产。20世纪80年代，在全球范围内掀起了高技术陶瓷产业化的热本文档来自技高网...

【技术保护点】
一种氧化锆注塑成型方法，其特征在于：以氧化锆粉末为主体，加入一定分量的有机载体，采用注射成型工艺制作坯体，通过合理的脱脂、烧结工艺制成高性能的氧化锆陶瓷制品。

【技术特征摘要】

【专利技术属性】
技术研发人员：王有才，
申请(专利权)人：湖南正阳精密陶瓷有限公司，
类型：发明
国别省市：43[中国|湖南]