用铝铬渣制成的蜂窝陶瓷原料及其制作蜂窝陶瓷的生产工艺制造技术

本发明专利技术公开了一种用铝铬渣制成蜂窝陶瓷原料，在铝铬渣细粉中加入铝铬渣细粉量６－１０％的粘结剂，用所述的用铝铬渣制成的蜂窝陶瓷原料制作蜂窝陶瓷的生产工艺：１）配料；２）混合球磨；３）加粘结剂和水捏合；４）进行真空练泥；５）挤压成型；６）干燥；７）烧成蜂窝陶瓷。本发明专利技术具有如下的有益效果，本发明专利技术是利用冶炼金属铬所产生的炉渣也称为铝铬渣生产蜂窝陶瓷，原料来源足，价格低，而且铝铬渣有优异的抗渣抗腐蚀性能，用其制作的蜂窝陶瓷质量性能好，使用寿命可以在１２－２４个月以上。

Honeycomb ceramic raw material made from aluminium chromium slag and process for producing honeycomb ceramic

The invention discloses an aluminum honeycomb ceramic material made of chromium slag, chromium slag binder in aluminum powder with aluminum chromium slag fine powder of 6 - 10%, the production process of ceramic honeycomb materials with the aluminum chromium slag made of making honeycomb ceramics: 1) 2) mixed ingredients; ball milling; 3) with binder and water kneading; 4) for vacuum extrusion molding; 5); 6) drying; 7) sintering of ceramic honeycomb. The invention has the advantages that the invention is produced by chromium metal smelting slag called aluminum chromium slag production of ceramic honeycomb, sources of raw materials, low price, and aluminum chromium slag has excellent anti slag corrosion resistance, with its production of ceramic honeycomb quality performance is good, service life can be preliminary a month.

【技术实现步骤摘要】

本专利技术涉及一种蜂窝陶瓷原料及其制作蜂窝陶瓷的生产工艺。
技术介绍
蜂窝陶瓷在环保节能领域是重要关键的部件，各厂家一直是采用抗热震性能好，耐火度较高的莫来石、堇青石或者添加刚玉等作为制作蜂窝陶瓷的最佳原料，由于莫来石、堇青石原料的抗渣抗腐性能不是很好，致使目前蜂窝陶瓷使用寿命很短，制作水平低的只能用6-8个月，质量好的也只能用10-12月，特别是那些炉温高过1300℃，或者使用脏煤气，SO2、CO、磷酸盐等腐蚀性物质高的情况下，有的蜂窝陶瓷投入使用一个月左右就粉化、坍塌了，或者被氧化铁渣全部粘死、堵死。
技术实现思路
本专利技术的目的是提供一种用铝铬渣制作蜂窝陶瓷的生产工艺。本专利技术的目的是通过如下方式实现的一种用铝铬渣制成的蜂窝陶瓷原料，在铝铬渣细粉中加入铝铬渣细粉量6-10％的粘结剂。也可以在铝铬渣细粉中加入铝铬渣细粉量1-80％的莫来石和6-10％的粘结剂。也可以在铝铬渣细粉中加入铝铬渣细粉量1-80％的堇青石和6-10％的粘结剂。也可以在铝铬渣细粉中加入铝铬渣细粉量1-80％的硅线石、红柱石、蓝晶石的三石混合物和6-10％的粘结剂。用以上所述的用铝铬渣制成的蜂窝陶瓷原料制本文档来自技高网...

【技术保护点】
一种用铝铬渣制成的蜂窝陶瓷原料，其特征在于：在铝铬渣细粉中加入铝铬渣细粉量６－１０％的粘结剂。