一种石墨基复合材料的制备方法技术

本发明专利技术提供一种石墨基复合材料的制备方法。将膨胀石墨粉与焦粉混合并压缩形成基体以石墨为主的石墨板，压制压力为５～５０ＭＰａ；用有机溶剂将沥青溶解，加入增强填料和催化石墨化填料，混合均匀，除去溶剂得到粘结剂混合物；将粘接剂混合物在１１０～１４０℃熔融，放入石墨板，施加的气体压力为１～５０ＭＰａ，浸渍１０～１２０分钟；取出浸渍的石墨板，冷却至室温，进行切割或破碎成小颗粒；将破碎后的混合物放入模具中压制成型。本发明专利技术使用价格低廉的膨胀石墨部分取代焦炭制备石墨复合材料，由于在原料中加入了增强填料和催化石墨化填料，因此在降低成本的同时仍可以制备具有优良的电性能、热性能、以及力学性能的石墨复合材料。

Method for preparing graphite base composite material

The present invention provides a preparation method of graphite matrix composite material. The expanded graphite plate graphite powder mixed with coke powder and graphite based matrix formed by compression, pressure is 5 ~ 50MPa; using organic solvent to dissolve asphalt, adding filler and Catalytic Graphitization of filler, mixing, removing the solvent to obtain the binder mixture; the adhesive mixture at 110 to 140 DEG C melting into the graphite plate and the air pressure is 1 ~ 50MPa, dipping 10 ~ 120 minutes; remove the impregnated graphite plate, cooling to room temperature, cut or broken into small particles; the mixture is crushed into the pressing mold. The invention uses cheap graphite replace coke preparation graphite composite material, because the raw materials in the reinforcing filler and Catalytic Graphitization of filler, therefore still can be prepared with excellent electrical properties, thermal properties and mechanical properties of the graphite composite material while reducing costs.

【技术实现步骤摘要】

【技术保护点】
一种石墨基复合材料的制备方法，其特征在于包括如下步骤：（１）将膨胀石墨粉与焦粉混合并压缩形成基体以石墨为主的石墨板，压制压力为５～５０ＭＰａ；（２）用有机溶剂例如苯、甲苯、四氢呋喃或碳酸丙稀酯将沥青溶解，加入增强填料和催化石 墨化填料，混合均匀，除去溶剂得到粘结剂混合物；（３）按重量百分比步骤１所制的石墨板６０％～８０％、步骤２所制的混合物２０％～４０％将步骤２所制得的混合物在１１０～１４０℃熔融，放入步骤１所制得的石墨板，施加的气体压力为１～５０ＭＰａ ，浸渍１０～１２０分钟；（４）取出浸渍的石墨板，冷却至室温，进行切割或破碎成小颗粒；（５）将步骤４所述的破碎后的混合物放入模具中压制成型。

【技术特征摘要】

【专利技术属性】
技术研发人员：魏彤，范壮军，
申请(专利权)人：哈尔滨工程大学，
类型：发明
国别省市：93[中国|哈尔滨]