A fly ash aggregate, which is characterized by selecting the carbon content of the volume ratio of 7% fly ash and water solution as masterbatch of fly ash ceramsite, the volume ratio of the carbon content of fly ash volume ratio of 7%: water = 99.8%: 0.02%; water solution by water glass, binder resin and water. The volume ratio of water glass: gel resin: water = 0.6%: 0.4%: 99%; the volume of carbon containing 7% fly ash and water solution of sufficient mixing, mixing uniformly spherical ball making machine, ball diameter is 10 20mm, and then into the open kiln, kiln used in drum fan led the firewood, blowing to kiln spontaneous combustion, fly ash burned the ball at the top of red light, stop the blast, until 40 minutes after the kiln, the flyash is made. The invention has the advantages of high content of fly ash and no clay component, low cost, good quality, simple process, small investment and easy implementation.
【技术实现步骤摘要】
本专利技术涉及一种建筑材料，具体地说是一种粉煤灰陶粒。二
技术介绍
遍布我国各地的大小热电厂及其它耗煤企业，每年产生大量的粉煤灰，加 上历年未及时处理的，对环境造成了日益严重的危害，而且越来越大的出灰量， 也给企业造成了巨大的经济负担，研制一种粉煤灰用量大的产品，不仅能使粉 煤灰变废为宝，得到充分的二次利用，减轻出灰企业的重负，降低用灰企业的 生产成本，更可以大大减少对环境的污染程度，近年来，我国出现了一些以粉 煤灰为原料的建筑材料，如中国专利《免烧免蒸砖及其制作方法》(专利号89109385.0，申请日89.12.16)，该专利技术由粉煤灰、煤渣(或粘土)、水泥、石 灰、外加剂组成，该专利技术的粉煤灰含量达20-65%，吃灰量大，免烧免蒸，与经 蒸养和焙烧的粉煤灰砖相比，具有设备投资少、易制作、成本低的优点，但在 制作中，辅料煤渣使用前须经破碎，使之粒径小于6mm，石灰要求也较高，石灰 中的过火石不能过多，有效氯化钙含量要大于65%，且使用前须经磨细(4900 孔筛不大于15%)，故制作工艺依然较复杂，而且原料中辅料的品种也较多，养 护时间也长达28天；又加已...
【技术保护点】
一种粉煤灰陶粒，其特征在于选用含碳量体积比为７％的粉煤灰和水溶液为粉煤灰陶粒的母料，体积比为含碳量体积比为７％的粉煤灰∶水溶液＝９９．８％∶０．０２％；水溶液由水玻璃、胶凝树脂和水组成，体积比为水玻璃∶胶凝树脂∶水＝０．６％∶０．４％∶９９％；将含碳量体积为７％的粉煤灰与水溶液充分搅拌混和，混合均匀后送入球形机进行制球，球径为１０－２０ｍｍ，再送入敞口窑中，在窑口用柴草引着，用鼓风机吹着自燃，待窑顶部粉煤灰球被烧的红透后，停止鼓风，待４０分钟后出窑，粉煤灰陶粒即制成。
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。