The invention belongs to the field of steel slag recovery and utilization, in particular to a method for making steel slag unburned brick. The technical scheme for the steel slag brick before need maintenance time, aging need pressure, high equipment costs, and handling operations such as links, large amount of labor, the further improvement of manpower and high cost problems, a method of making the steel slag brick is the raw material of steel slag sand, steel slag powder the blast furnace slag and lime, in two or more than two kinds of materials weighing well into the blender, add water, stir, feeding to the press were pressed, and then pressing the brick directly under normal pressure of aging, industrial exhaust gas containing CO: 2 access in aging in Chen, by the end of the finished steel slag brick, this method does not require maintenance time, during the aging process without pressure, low requirement for the equipment, and the direct use of the waste heat of the exhaust gas, reduce the cost.
【技术实现步骤摘要】
本专利技术属于钢渣的回收利用领域，具体为 。 背景纟支术钢渣是炼钢过程中排出的熔渣，主要是金属炉料中各元素被氧化后生成的 氧化物、被侵蚀的炉衬料和补炉材料、金属炉料带入的杂质和为冶炼不同钢种 需要而特意加入的石灰石、白云石、铁矿石、萤石等造渣材料。钢渣占钢铁工业固体废物的15~20%，每生产1吨粗钢都会排放约180Kg的钢渣，我国积存 钢渣已有2亿吨以上，占地l万多亩，大量的钢渣，不仅侵占土地，而且钢渣 在堆放过程中易于风化成碱性粉尘，对周围的环境造成严重的污染。目前钢渣 主要在建筑材料领域有所应用，如生产钢渣水泥、做水泥配合料、钢渣微粉、 地基材料等，但利用率较低，仅占10°/。左右，且每年仍以数百万吨的排渣量递 增，如果不对其进行处理和综合利用，将会占用越来越多的土地，在形成环境 污染的同时也造成大量可利用资源的浪费，从而影响到钢铁工业的可持续发展。 本申请人已于08. 1.21日申请了一份名称为"一种钢渣免烧砖"的专利申 请，其申请号为200810014015.8 ，该文件中公开了 一种钢渣免烧砖，所述的钢 渣免烧砖的原料包括钢渣砂、钢渣粉、高炉渣、石...
【技术保护点】
一种钢渣免烧砖的制作方法，将原料钢渣砂、钢渣粉、高炉渣、石灰中的两种或者两种以上物料称量好送入搅拌机，加入水，搅拌均匀后，上料至压砖机进行成型压制，其特征在于，压制成型的砖直接在常压下进行陈化，在陈化中通入含ＣＯ↓［２］的工业尾气，陈化结束得到成品钢渣免烧砖。
【技术特征摘要】
【专利技术属性】
技术研发人员：罗时政，亓立峰，刘富增，郑文军，宋青伟，马晓健，常均，王玺，胡玉芬，韩明年，陈东玫，庄健，赵爱新，
申请(专利权)人：济南鲍德炉料有限公司，
类型：发明
国别省市：88[中国|济南]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。