The invention belongs to the technical field of ceramics and refractory materials, in particular to a method for producing high-quality synthetic refractory materials. The technical scheme of the invention includes: the homogenization process, the crushing dry grinding process, the wet grinding and pulping process and the flotation process, the process of the mud filter, stale, dry process and the calcination process. According to the different products with different grade pulp production, Al: 2 O: 3. The content of 71 ~ 79% production of high aluminum homogenizing material; Al: 2 O: 3. The content of 80 ~ 83% production of high aluminum homogenizing material based sintered corundum, by flotation tailings and kaolin slurry the production of sintered mullite ore blending. The effect of the invention is that the pre homogenization method is adopted to improve the stability of the raw material components in the after process, thereby greatly reducing the workload of process control in the whole production process. Using flotation process, vacuum hard plastic extrusion equipment, pre burning process and other methods, the use of medium and low-grade ore to produce high-quality, high-quality raw materials of synthetic refractories.
【技术实现步骤摘要】
本专利技术属于陶瓷、耐火材料
，特别是涉及。
技术介绍
我国的砜土生产开始于二十世纪五十年代， 一直采用原矿直接入窑烧成的方式。而原矿 品位的高低，直接制约了产品的品质。我国出口矾土，基本是AlA大于85。/。的高品位矾土熟 料，而这部分资源只占总储量的百分之几，大量的中、低品位资源得不到充分利用。目前优 质高品位(AL03含量高)矿日渐贫乏，低品位(a;uo3含量低)、复杂难处理矿无人问津。针 对国内大量的中、低品位铝矾土资源，提供新型生产加工方法。可以使较低品位原矿石，生 产优质合成耐火材料。是目前主要研究的方向。
技术实现思路
本专利技术的目的是针对国内大量的中、低品位铝矾土资源，提供一种新型生产加工方法。 这种方法可以使用较低品位原矿石，生产优质合成耐火材料。本专利技术的优质合成耐火材料技术方案是包括①均化破碎工序、②干法粉磨工序、③湿 磨制浆工序、 浮选工序、⑤压滤、陈腐工序⑥挤泥、干燥工序和⑦煅烧工序。所述的均化破碎工序是用装载机在不同的Al203含量料堆抓取原料，在均化棚中形成均 化料堆；将均化料堆的料，通过粗碎与细碎两级鄂破，将块度为300mr...
【技术保护点】
优质合成耐火材料的生产方法，其特征是包括①均化破碎工序、②干法粉磨工序、③湿磨制浆工序、④浮选工序、⑤压滤、陈腐工序⑥挤泥、干燥工序和⑦煅烧工序。
【技术特征摘要】
【专利技术属性】
技术研发人员：刘海坚，胡建生，赵成美，
申请(专利权)人：天津泽希矿产加工有限公司，
类型：发明
国别省市：12[中国|天津]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。