The invention discloses a negative temperature coefficient thermistor dual phase composite material and a preparation method thereof, which is characterized by copper acetate, oxalate iron, manganese acetate, nickel acetate and oxalic acid molar of 0.2 to 0.6: 1: 3.48 to 3.08: 1.32: 7.2 mixing ball milling, drying after calcination, the resulting powder and partially stabilized cubic zirconia powder 1: 1.5 to 4 molar mixing, milling drying, double phase composite powder by sintering, relative density of negative temperature coefficient materials more than 94% is obtained. The stable structure, sintering temperature at 1200 to 1250 DEG C, the mechanical strength is higher than that of 2800K single phase spinel ceramics, B, resistivity of 1000 ohm.Cm, 150 DEG C accelerated aging resistance drift is less than 3% 1000h, and has very good characteristics in NTC - 60 DEG C to 50 DEG C temperature range, can be used for negative temperature the coefficient of thermal sensor material in modern high altitude balloon.
【技术实现步骤摘要】
本专利技术属于负温度系数热敏材料
，特别涉及一类应用在现代高空气球中的 负温度系数(NTC)双相复合热敏传感器材料及其制备方法。技术背景尖晶石结构化合物是一种常用的NTC材料，鉴于这类材料的电阻率关于温度具有阿 伦尼乌斯(Arrhenius)关系R=R。exp (B/T),式中R。为温度趋向无穷大材料的电导率(Q . CHI ), B为热敏常数(K )， T为绝对温度(K )，所以这种材料可以用来作为负系数热敏电阻器。现有负温度系数热敏电阻器大部分是用尖晶石型半导体陶瓷制成的，以采 用Mn-Cu-Ni-0系、Mn-Co-Ni-0系或Mn-Fe-Ni-0系等含Mn尖晶石结构陶资最为广泛。其 中有一部分负温度系数热敏电阻器在介于常温和低温之间工作，如现代高空科学气球中 用到的负温度系数热敏电阻器， 一般工作在高度30 - 40千米的平流层，工作温度为-55 。C左右；这类NTC材料不同于低温NTC材料要求"低电阻率低B值"，也不同于常温NTC 材料要求"中等电阻率中等B值"，而是要求有中等的电阻率和相对较低的B值， 一般要 求B值低于2800 K，电阻率不...
【技术保护点】
一种负温度系数双相复合热敏材料的制备方法，其特征在于：先将乙酸铜、草酸铁、乙酸锰、乙酸镍和草酸按摩尔比为０．２～０．６∶１∶３．４８～３．０８∶１．３２∶７．２混合球磨１２～２４ｈ，烘干后，在８００～８５０℃空气气氛下煅烧２～４ｈ，得到单相粉体；将该单相粉体：部分稳定的立方氧化锆粉体按摩尔比１∶１．５～４混合，球磨混合１～２天，烘干，制得双相复合物粉体；将该制得的粉体成型，在２００～３００Ｍｐａ冷等静压下压制成生坯，以３～１０℃／ｍｉｎ加热到１２００～１２５０℃烧结并保温３００～３６０ｍｉｎ，随炉冷却，即得到负温度系数双相复合热敏陶瓷材料。
【技术特征摘要】
【专利技术属性】
技术研发人员：罗伟，杨萍华，朱运兵，陈初升，刘原平，
申请(专利权)人：合肥三晶电子有限公司，中国科学技术大学，
类型：发明
国别省市：34[中国|安徽]