The invention discloses a method for glazed red glaze porcelain, which comprises the following steps: 1) by using 1100 - 1300 DEG C firing package type high temperature red glaze ceramic glaze as a blank; 2) take ceramic pigment powder according to the total mass of 5 - 50% add transparent base glaze powder pigment powder. The mixture with a mass ratio of 70% camphor oil of frankincense oil and 30% composition of the powder pigment made of paste pigment; 3) with step 2) pigment in the glaze body painting pattern or printed pattern on body glaze Decal Decals painted made of semi-finished products; 4) step 3) painted half refined natural dried into the furnace in the temperature of 1050 to 1250 DEG C under the burning of finished products. The utility model has the advantages that the decorative pigment is completely glazed, and the surface is smooth and smooth; the decorative part is fully glazed, and the abrasion resistance is greatly improved than that of the glaze color; the amount of the lead dissolution is greatly reduced than that of the glaze color.
【技术实现步骤摘要】
本专利技术属于陶瓷釉面彩绘方法，具体涉及一种用于大红釉面瓷的 釉中彩方法。
技术介绍
中国历史上发展过多种类似红色的釉用陶瓷色料，如桔红色的铁 红、紫红色的锰红、酱红色的铜红等，而真正意义上的大红色色料目 前只有现代人工合成的硫硒化镉(简称硒镉红) 一种，近年来科研人 员和生产企业围绕硒镉红在陶瓷生产上的应用做了大量工作。硒镉红合成时是一种粉红色固体，若配以适当基础釉经60(TC以 上烧制可成为大红色釉面，但其热稳定性不好，60(TC以上即开始分 解，这与生产上通常要求的100(TC以上的成釉温度有较大差距。多 年以来生产和科研人员都在致力于提高硒镉红的热稳定性以制成高 温红色釉料，目前主要应用的有缓分解中温红釉(烧成温度约1050 "C)和高温包裹大红釉，高温包裹釉就是一种比较成熟的技术。该技 术主要针对硒镉红易分解的问题，用高温下稳定的硅酸锆晶体包裹硒 镉红以提高其热稳定性，并以此为色料制成高温大红釉取得成功。这 种釉料对烧制窑具要求不严，烧制温度达到110(TC—130(TC，可工 业化生产，釉面平整细腻，由于釉面质量高，为进行后期的艺术加工 创造了良好...
【技术保护点】
一种用于大红釉面瓷的釉中彩方法，包括以下步骤： １）选用经１１００－１３００℃烧制的包裹型高温大红色釉陶瓷作为色釉胚体； ２）取陶瓷色料粉按总质量的５－５０％添加透明基础釉粉配制颜料粉，再用质量配比为７０％的乳香油和３０％的樟脑油组成的混合物将颜料粉调制成糊状颜料； ３）用步骤２）的颜料在色釉胚体上彩绘图案或印成花纸图案在色釉胚体上贴花制成彩绘半成品； ４）将步骤３）的彩绘半成品自然风干后入炉，在炉温１０５０－１２５０℃下烧制成成品。
【技术特征摘要】
【专利技术属性】
技术研发人员：姜旭，傅涛，王伟生，
申请(专利权)人：傅涛，
类型：发明
国别省市：43[中国|湖南]