高折射率镧系光学玻璃LaSF015制造技术

本发明专利技术公开了一种高折射率镧系光学玻璃ＬａＳＦ↓［０１５］及其生产工艺，按重量百分比计量的组份为ＳｉＯ↓［２］４．５－７．５％、Ｂ↓［２］Ｏ↓［３］２０－２４％、Ｌａ↓［２］Ｏ↓［３］２９－３４％、ＺｒＯ↓［２］４．５－７．５％、Ｔａ↓［２］Ｏ↓［５］３－１３％、ＷＯ↓［３］０－１．５％、ＴｉＯ↓［２］０－１．５％、Ｇｄ↓［２］Ｏ↓［３］１８－３２％。将上述组份混合，经１４５０℃－１４８０℃熔制、１３００℃出炉，成型，检验，再经６５０℃－７００℃，退火８－１０天。是用于制造高级照相机，高级精密仪器等高折射率低色散的镧系光学玻璃。（*该技术在2023年保护过期，可自由使用*）

High refractive index lanthanide optical glass LaSF015

The invention discloses a high refractive index lanthanide optical glass LaSF down 015 and its production process, according to the weight percentage of the measurement components for SiO: 2, B: 4.5 - 7.5% 2 O: 3, La: 20 - 24% 2 O: 3 29 34%, ZrO: 2, Ta: 4.5 - 7.5% - 2 O: 5 313%, WO: 3, TiO: 2 01.5% 01.5%, Gd: 2 O: 3 1832%. The components are mixed and melted at 1450 - 1480 DEG C, annealed at 1300 degrees, and tested, then annealed for 8-10 days at 650 - 700 DEG C. It is a kind of optical glass with high refractive index and low dispersion for advanced camera, advanced precision instrument and so on.

【技术实现步骤摘要】

本专利技术是重镧火石玻璃大类中一个牌号，是制造数码相机、数码摄像机、CDROM、扫描仪及其他数码光电产品读写镜头必需的配套材料，同时也被广泛地应用于航空、航天等高折射率低色散镧系玻璃。
技术介绍
LaSF015重镧火石光学玻璃其组成系统有SiO2、B2O3、La2O3、Gd2O3、ZrO2、Ta2O5、Y2O3。上述配方中Ta2O5对玻璃析晶影响较大，含量太高成本高，太低会影响析晶及成型性能。
技术实现思路
本专利技术的目的在于提供一种光学系数nd、vd，析晶性能，成型性能良好的，成本低的一种高折射率低色散的重镧火石玻璃。本专利技术在选择了SiO2、B2O3、La2O3、ZrO2、Ta2O5、Y2O3、Gd2O3、系统基础上，将配方中用Gd2O3取代部分Ta2O5，增加WO3，TiO2等氧化物，调整各组份配方，采用熔制、成型、退火、检验、性能测试工艺步骤来实现其目的。本专利技术的高折射率镧系光学玻璃LaSF015，按重量份计量的组份为高折射率镧系光学玻璃(LaSF015)，其特征是按重量百分比计量的组份为SiO24.5-7.5％、B2O320-24％、La2O329-34％、ZrO2本文档来自技高网...

【技术保护点】
一种高折射率镧系光学玻璃ＬａＳＦ↓［０１５］，其特征是按重量百分比计量的组份为ＳｉＯ↓［２］４．５－７．５％、Ｂ↓［２］Ｏ↓［３］２０－２４％、Ｌａ↓［２］Ｏ↓［３］２９－３４％、ＺｒＯ↓［２］４．５－７．５％、Ｔａ↓［２］Ｏ↓［５］３－１３％、ＷＯ↓［３］０－１．５％、ＴｉＯ↓［２］０－１．５％、Ｇｄ↓［２］Ｏ↓［３］１８－３２％。

【技术特征摘要】

【专利技术属性】
技术研发人员：王佩珍，
申请(专利权)人：上海新沪玻璃厂，
类型：发明
国别省市：31[中国|上海]