中温陶瓷大红釉制造技术
Medium temperature ceramic red glaze
A medium temperature ceramic red glaze, by PbO B: 2 O: 3 SiO: 2 of base glaze and colorant composition, which is characterized in that the weight percentage of the amount of base glaze composition are: lead 40 ~ 50%, 25 ~ 28% silica oxide three, two B 6 ~ 8%, three ~ 5.5% 4 two aluminum oxide, calcium peroxide 4 ~ 6%, Zinc Oxide 6 ~ 8%, 4 ~ 7% wt% K2O; dosage of the colorant composition are: silica 37 ~ 45%, two ~ 25% three 22 zirconia, two aluminum oxide from 6 to 10%, three and two of boron oxide from 4 to 6%, 6 to 9% lead, Zinc Oxide 4 ~ 6%, 7 ~ 9% CdSe CDs, 1 ~ 2.5%. The ceramic red red glaze, suitable for porcelain in 1170 ~ 1210 DEG C, oxidizing flame firing a medium temperature glaze environment, rapid temperature, especially suitable for roller kiln, one-time glaze firing process application.
【技术实现步骤摘要】
本专利技术涉及一种，尤其是指适用于炻瓷类制品的色釉，属于釉类配制方法类。
技术介绍
大红釉是陶瓷釉色中极难研制的釉色品种，尤其对于色泽如红辣椒般鲜艳夺目的大红色釉更是难得。古往今来，陶瓷行业中的大多数同行都采用氧化铜作为制作红色釉的主要显色料，让其在还原烧成环境下获得；但由于还原烧成环境难以控制，故而使呈色效果极不稳定；因此至今仍无十分理想的、能用于炻瓷类制品的如红辣椒色泽般的大红釉。
技术实现思路
本专利技术的目的旨在提供一种能使坯釉在1170℃～1210℃一次性烧成的大红色釉，为陶瓷产品提供一种稳定性好、烧成色泽如红辣椒般光鲜亮丽的中温陶瓷用釉。这种中温陶瓷用红釉，它由PbO-B2O3-SiO2系基础釉和着色剂组成，其特征在于A、所述基础釉组成物的重量百分比用量分别是氧化铅40～45％，二氧化硅25～28％，三氧化二硼6～7％，三氧化二铝4～5.5％，二氧化钙4～6％，氧化锌6～8％，氧化钾4～7％。B、所述着色剂组成物的重量百分比用量分别是二氧化硅37～45％，二氧化锆22～25％，三氧化二铝6～10％，三氧化二硼4～6％，氧化铅6～9％，氧化锌4～6％，硒...
【技术保护点】
一种中温陶瓷大红釉，它由ＰｂＯ－Ｂ↓［２］Ｏ↓［３］－ＳｉＯ↓［２］基础釉、着色剂和外加料组成，其特征在于：Ａ、述基础釉组成物的重量百分比用量分别是：氧化铅４０～４５％，二氧化硅２５～２８％，三氧化二硼６～７％，三氧化二铝４～５．５％，二氧化钙４～６％，氧化锌６～８％，氧化钠２～４，氧化钾５～７％；Ｂ、所述着色剂组成物的重量百分比用量分别是：二氧化硅３７～４５％，二氧化锆２２～２５％，三氧化二铝６～１０％，三氧化二硼４～６％，氧化铅６～９％，氧化锌４～６％，硒化镉７～９％，硫化镉１～２．５％；Ｃ、所述的外加料是具高岺土性状的粘土－龙岩土和二氧化硅。
【技术特征摘要】
【专利技术属性】
技术研发人员：刘锡泉，李秋明，
申请(专利权)人：湖南省天博瓷业有限公司，
类型：发明
国别省市：43[中国|湖南]
-
0来自[天津市电信IDC机房] 2015年03月15日 01:211.即大功。丧服名。2.中国传统色彩名称，即正红色，三原色中的红，传统的中国红