玻璃彩釉用无铅镉、高稳定性低熔点玻璃制造技术

一种用于玻璃彩釉用无铅镉钡等有毒重金属的低熔点玻璃，所述玻璃的组成为：５－４０ｗｔ％ＳｉＯ↓［２］，１－４０ｗｔ％Ｂ↓［２］Ｏ↓［３］，０－４５ｗｔ％ＺｎＯ，０－１５ｗｔ％ＣａＯ，０－１５ｗｔ％ＭｇＯ，０－５ｗｔ％ＣａＦ↓［２］，０－２０ｗｔ％Ｎａ↓［２］Ｏ，０－２０ｗｔ％Ｋ↓［２］Ｏ，０－１０ｗｔ％Ｌｉ↓［２］Ｏ，０－２５ｗｔ％ＴｉＯ↓［２］，０－５ｗｔ％ＺｒＯ↓［２］，０－５ｗｔ％Ａｌ↓［２］Ｏ↓［３］，０－３０ｗｔ％ＭｏＯ↓［３］，０－５０ｗｔ％Ｂｉ↓［２］Ｏ↓［３］，０－４０ｗｔ％Ｓｂ↓［２］Ｏ↓［３］，其特征是不含铅镉钡等有毒重金属，同时其化学稳定性好，膨胀系数（３０－３００℃）在７５－９５×１０↑［－７］／℃之间和使用温度５００－７２０℃。

Glass glaze with lead-free cadmium, high stability and low melting point glass

For a low melting point glass of toxic heavy metals such as barium lead and cadmium free glass glaze composition, the glass is: 5 40wt%SiO: 2, 40wt%B: 1 - 2: O 3, 0 45wt%ZnO, 0 15wt%CaO, 0 15wt%MgO, 0 5wt%CaF: 2 0, 20wt%Na: 2 O, 020wt%K: 2 O, 010wt%Li: 2 O, 025wt%TiO down 2, 05wt%ZrO down 2, 05wt%Al down 2 O down 3, 030wt%MoO down 3, 050wt%Bi down 2 O down 3. 040wt%Sb Case 2: O 3, which is characterized in that the lead cadmium and barium, while its chemical stability, thermal expansion coefficient (30 - 300 DEG C) in the 75 - 95 * 10 = - 7 / C, and the use of temperature between 500 - 720 DEG C.

【技术实现步骤摘要】
所属
本技术涉及一种应用于玻璃彩釉的低熔点玻璃，作为无机色料与玻璃之间的粘结剂，该玻璃的最大特点是不含铅镉等有毒重金属，并且化学稳定性好。
技术介绍
彩釉是一种应用在玻璃、陶瓷表面装饰的特种油墨；一般由低熔点玻璃、颜料和调墨油三部分组成。彩釉玻璃是在普通平板玻璃、瓶罐玻璃、艺术玻璃、磨光玻璃、压延玻璃或玻璃砖表面涂敷一层彩色易熔釉，也可以通过丝网或辊筒印刷机印制在浮法玻璃表面，在培烧炉或者钢化炉中加热至适当温度，使釉层熔融并与玻璃粘结，再经过退火或者风冷钢化而形成的产品。这种玻璃具有良好的耐久性、耐热反射性和耐水性，色彩稳定不脱落。适用于室内饰面层、一般建筑物门厅和楼梯间的饰面层及建筑物外饰面层，最近彩釉玻璃已经大量应用到煤气灶、微波炉和冰箱等家用电器行业以及汽车玻璃行业中，每年的产值超过几百亿。随着社会的进步和人们生活水平的提高，人们的审美观的越来越高，玻璃彩釉装饰品的需求也会越来越多。传统的彩釉基本上都含有氧化铅、氧化镉等有害重金属，众所周知，被吸收的铅排泄非常缓慢，即使摄取少量，也不能完全排泄于体外而一部分残留于体内，首先铅进入循环血液中，一部份排泄于尿中，大部份经大小肠而排本文档来自技高网...

【技术保护点】
一种用于玻璃彩釉用无铅镉钡等有毒重金属的低熔点玻璃，所述玻璃的组成为：５－４０ｗｔ％ＳｉＯ↓［２］，１－３０ｗｔ％Ｂ↓［２］Ｏ↓［３］，０－４５ｗｔ％ＺｎＯ，０－１５ｗｔ％ＣａＯ，０－１５ｗｔ％ＭｇＯ，０－５ｗｔ％ＣａＦ↓［２］，０ －２０ｗｔ％Ｎａ↓［２］Ｏ，０－２０ｗｔ％Ｋ↓［２］Ｏ，０－１０ｗｔ％Ｌｉ↓［２］Ｏ，０－２５ｗｔ％ＴｉＯ↓［２］，０－５ｗｔ％ＺｒＯ↓［２］，０－５ｗｔ％Ａｌ↓［２］Ｏ↓［３］，０－３０ｗｔ％ＭｏＯ↓［３］，０－５０ｗｔ％Ｂｉ↓［２］Ｏ↓［３］，０－４０ｗｔ％Ｓｂ↓［２］Ｏ↓［３］，其特征是不含铅镉钡等有毒重金属，同时其化学稳定性好，膨胀系数和使用...

【技术特征摘要】

【专利技术属性】
技术研发人员：王德强，潘伟，郑金标，
申请(专利权)人：王德强，潘伟，郑金标，
类型：发明
国别省市：31[中国|上海]