The invention relates to a method for preparing bismuth oxide film, relating to a preparation method. The method solves the problems of complicated operation, high cost, complicated phase composition and uneven film layer in the preparation of bismuth oxide film. The method comprises the following steps: A, Bi (NO: 3): 3.5H: 2 O dissolved in nitric acid solution, then PEG200 and citric acid was added into the above solution, stirring evenly; after B, to join OP, step a solution after treatment in stirring the solution is made of sol; C, the cleaned ordinary glass substrate prepared by immersion, soak 1 to 15 minutes, with 1 ~ 10cm / min speed lifting glass; D, the glass steps after C treatment in an oven drying; drying e, a piece of glass after placed in a muffle furnace, sintering at different temperatures, a piece of glass after sintering natural cooling to room temperature, the glass sheet made of bismuth oxide thin films. The invention has the advantages of simple operation, low cost, simple phase composition and uniform film layer.
【技术实现步骤摘要】
本专利技术涉及一种制备方法。
技术介绍
氧化铋是一种先进的功能材料，是最重要的铋化合物之一。氧化铋既具有共价键的特性，又具有金属键的特性；这种结构使氧化铋具有介电性能优良、反射指数高，折射率高，禁带宽度宽(2～3.96Ev)，光导和光致发光特性良好等许多独特的物理性能。氧化铋主要以α、β、γ、δ和ω等五种晶型存在，晶型不同，应用不同。其中，低温烧结而成的α相氧化铋相对稳定，应用比较广泛。由氧化铋组成的薄膜型材料已广泛应用于电子陶瓷材料、电解质材料、光电材料、传感器、导电玻璃、高温超导材料、有毒气体探测等领域中。目前，氧化铋薄膜的制备方法主要有化学气相沉积法、溅射法、脉冲激光沉积法、真空喷镀法、常压卤化物化学蒸汽沉积法等方法。但是这些方法制备氧化铋薄膜存在操作复杂、成本高、相组成复杂和膜层不均匀等缺点，难以满足高性能新型材料的要求。近年来，国外报道一种以有机物三(2，2′-6，6′-四甲基庚烷-3，5-聚酯)合铋为前驱体，用溶胶-凝胶法制备氧化铋薄膜的方法。但该法的主要问题是原料成本较高，不适合工业化生产。
技术实现思路
本专利技术是为了解决目前制备氧化铋薄膜的方法...
【技术保护点】
一种制备氧化铋薄膜的方法，其特征在于制备方法如下：ａ、将１～１０ｇ的Ｂｉ（ＮＯ↓［３］）↓［３］.５Ｈ↓［２］Ｏ溶解在ＨＮＯ↓［３］∶Ｈ↓［２］Ｏ体积比为１∶２～１∶２０的硝酸溶液１０～１００ｍｌ中，再将１～５ｇ的ＰＥＧ２００和１～１０ｇ柠檬酸加入到上述溶液中，搅拌均匀；ｂ、向经步骤ａ处理后的溶液中加入０．２～２．０ｇ的ＯＰ，搅拌１～１０小时，即将上述溶液制成了溶胶；ｃ、将清洗好的普通玻璃片浸入制好的溶胶中，浸泡１～１５分钟后，以１～１０ｃｍ／ｍｉｎ的速度提拉玻璃片；ｄ、将经步骤ｃ处理后的玻璃片在５０～１５０℃的烘箱中烘干；ｅ、将烘干后的玻璃片放在马弗炉中进行烧结，将马弗炉...
【技术特征摘要】
【专利技术属性】
技术研发人员：吴晓宏，秦伟，何伟东，王松，
申请(专利权)人：哈尔滨工业大学，
类型：发明
国别省市：93[中国|哈尔滨]