浮法在线生产阳光控制镀膜玻璃的方法技术

本发明专利技术涉及浮法在线生产阳光控制镀膜玻璃的方法。利用金属有机化合物化学气相沉积法，在浮法玻璃生产线的退火窑Ａ０区，温度在５５０～６００℃范围内，在热的玻璃带表面沉积含钛源，掺磷和碳的具有阳光控制功能的膜层。与现有的阳光控制镀膜玻璃相比，该镀膜玻璃具有可见光透射比高、可见光反射比低、耐磨性好、热加工前处理简单的特点。

Float on-line production method for controlling coated glass by sunlight

The invention relates to a method for float on-line production of sunlight controlled coated glass. Deposition method using metal organic chemical gas, A0 annealing furnace in float glass production line, the temperature at 550 to 600 DEG C, in the heat of the glass surface deposition of titanium containing phosphorus doped carbon source, and the sun has the control function of the film. Compared with the existing sunlight controlled coating glass, the coated glass has the characteristics of high visible light transmittance, low visible light reflection ratio, good abrasion resistance, simple heat treatment and simple pretreatment.

【技术实现步骤摘要】

【技术保护点】
浮法在线生产阳光控制镀膜玻璃的方法，其特征在于它包括以下步骤：在浮法玻璃生产线退火窑的Ａ０区，温度为５５０～６００℃的玻璃带上方设置单进气通道、双侧排气的镀膜反应器，利用金属有机化合物化学气相沉积法，以氮气或氩气为载气，将已被汽化预混合的含钛源、掺杂剂的前质体汽体，输送到移动的浮法玻璃带表面，进行热分解形成具有阳光控制的二氧化钛膜层，所说的掺杂剂为磷源和碳源，前质体汽体混合物的摩尔百分比为钛源０．１～１．２ｍｏｌ％，磷源０．００１～０．０２ｍｏｌ％，碳源０．００１～０．０５ｍｏｌ％，其余为氮气或氩气。

【技术特征摘要】

【专利技术属性】
技术研发人员：刘军波，刘起英，应益明，曹涯雁，赵年伟，陈华，莫建良，汪建勋，孔繁华，赵明，张铫，施燕飞，
申请(专利权)人：杭州蓝星新材料技术有限公司，
类型：发明
国别省市：86[中国|杭州]