The present invention provides a kind of acid and alkali in harsh environment of long glass fiber reinforced PP material and preparation method thereof, by adding an appropriate amount of copper acetate and five water sodium thiosulfate can effectively enhance the corrosion resistance of long glass fiber reinforced PP composite, long glass fiber. The invention provides enhanced PP composite materials in harsh pH in the environment in the use of the surface is not easy pulverization, maintain high notched impact strength of the long term, especially suitable for the preparation of instrument shell, corrosion resistance can require higher spacecraft interiors, car interiors, ship interiors, electrical enclosures.
【技术实现步骤摘要】
本专利技术涉及材料
,具体涉及一种高抗冲防静电长玻纤增强PP材料及其制备方法和应用。
技术介绍
长玻纤增强聚丙烯(LFRT-PP)材料具有优异的耐冲击性以及优良的力学性能和电绝缘性,其使用温度范围一般在-100~160℃之间,尺寸稳定性高,耐蠕变性高,是一种集刚、硬、韧于一体的典型塑料。正是由于这些优点,聚玻纤增强PP现已被广泛应用于电子电器、办公用品、精密机器、医疗、劳保、家庭用品以及汽车等领域。长玻璃纤维增强聚丙烯树脂作为一种具有前沿技术特点的优良产品,其拥有强度高、耐化学性优异等显著优点,对于该产品的开发研究具有重要的市场价值,对促进国民经济的发展起到重要作用。但现有的长玻纤增强PP复合材料酸碱苛刻条件的耐受性较差,在酸性或碱性条件下容易变性而脆化,缺口抗冲击性能下降。当这种材料被用于生产电子电气元件、航空器零部件、通信部件时,产品外壳容易破损,使用寿命较短。
技术实现思路
有鉴于此,本专利技术公开一种耐酸碱苛刻环境的长玻纤增强PP复合材料。本专利技术的目的通过以下技术方案实现:一种耐酸碱苛刻环境的长玻纤增强PP复合材料,其原料按重量计包括:PP70-95份;长玻纤20-30份;抗氧化剂0.2-0.7份;抗紫外线剂0.1-0.4份;阻燃剂0.5-1.5份;五水硫代硫酸钠0.03-0.08份;一水合醋酸铜0.05-0.09份。所述PP可选用任意一种聚丙烯树脂实 ...
【技术保护点】
一种耐酸碱苛刻环境的长玻纤增强PP复合材料,其原料按重量计包括:PP 70‑95份;长玻纤 20‑30份;抗氧化剂 0.2‑0.7份;抗紫外线剂 0.1‑0.4份;阻燃剂 0.5‑1.5份;五水硫代硫酸钠 0.03‑0.08份;一水合醋酸铜 0.05‑0.09份。
【技术特征摘要】
1.一种耐酸碱苛刻环境的长玻纤增强PP复合材料,其原料按重量计包括:
PP70-95份;
长玻纤20-30份;
抗氧化剂0.2-0.7份;
抗紫外线剂0.1-0.4份;
阻燃剂0.5-1.5份;
五水硫代硫酸钠0.03-0.08份;
一水合醋酸铜0.05-0.09份。
2.根据权利要求1所述的耐酸碱苛刻环境的长玻纤增强PP复合材料,其特征在于:所述
长玻纤为无碱连续长玻纤,所述无碱连续玻纤直径为11-20μm。
3.根据权利要求1所述的耐酸碱苛刻环境的长玻纤增强PP复合材料,其特征在于:所述
抗氧化剂为抗氧剂1010。
4.根据权利要求1所述的耐酸碱苛刻环境的长玻纤增强PP复合材料,其特征在于:所述
抗紫外线剂为紫外线吸收剂UV-234。
5...