一种户外木器涂装工艺制造技术

本发明专利技术提供了一种户外木器涂装工艺，其特征在于，包括如下步骤：确保木材含水率＜10%；封闭底漆按甲、乙、丙组份按比例开稀；通过喷/刷涂施工，先用封闭底漆对白坯完全封闭两遍；待漆膜干燥后，打磨清理干净后，中涂底漆甲、乙、丙组份按比例开稀后，通过喷/刷涂施工；待漆膜干燥后，通过层间打磨重涂来刷出漆膜丰满度；待漆膜做出丰满度后，哑光面漆甲、乙、丙组份按比例开稀后，通过喷/刷涂施工；待漆膜干燥后漆膜干燥后，通过层间打磨重涂来刷出漆膜丰满度；完成面漆涂刷后，应确保漆膜完成干燥前不受外界触碰。经检测和试用证明，其涂层附着力强、柔韧性好、硬度高、遮盖力好、高光泽，能显著提高漆膜涂装长期使用时的耐磨耐划性能。

Outdoor wood coating process

The present invention provides an outdoor wood coating process, characterized by comprising the following steps: to ensure that the wood moisture content is less than 10%; primer by a, B and C group according to the proportion of thinning; through the spray / brush construction, with closed primer on tofo completely closed two times; the paint film after drying after cleaning, polishing, coating primer a, B and C group according to proportion after thinning, the spray / brush construction; the film after drying, to film fullness out of the brush by layer grinding heavy coating; to make film fullness, matte finish a, B and C according to the proportion after thinning, the spray / brush construction; for the film after drying the film after drying, to film fullness out of the brush by layer grinding re coating; finish topcoat after brushing, should ensure that the film is not affected by external touch before drying is completed. The test and trial show that the coating has good adhesion, good flexibility, high hardness, good hiding power, high gloss, and can significantly improve the wear resistance and wear resistance of the coating when used for a long time.

【技术实现步骤摘要】

本专利技术涉及一种户外木器涂装工艺。
技术介绍
户外用木器清漆由三层，即封闭底漆、中途底漆和面漆构成，封闭底漆具有渗透性强、封闭性能优异等特点，直接附着于基材表面，可提高基底强度，中途底漆用于加强面漆的粘合力，使得面漆更加丰满细腻和圆滑，同时还具有防腐蚀作用，面漆是涂装的最终涂层，装修或刷漆后所呈现出的漆面效果由面漆呈现。但是，传统工艺中木器涂装后涂层附着力、柔韧性、硬度、遮盖力、耐磨耐划性能等在某些环境特别是户外环境下并不能尽如人意。
技术实现思路
为了克服上述现有技术的不足，本专利技术提供一种户外木器涂装工艺，涂装后涂层附着力强、柔韧性好、硬度高、遮盖力好、高光泽，能显著提高漆膜涂装长期使用时的耐磨耐划性能。本专利技术解决其技术问题所采用的技术方案是：一种户外木器涂装工艺，其特征在于，包括如下步骤：A、确保木材含水率＜10%；B、封闭底漆按甲、乙、丙组份按比例开稀；C、通过喷/刷涂施工，先用封闭底漆对白坯完全封闭两遍；D、待漆膜干燥后，打磨清理干净后，中涂底漆甲、乙、丙组份按比例开稀后，通过喷/刷涂施工；E、待漆膜干燥后，通过层间打磨重涂来刷出漆膜丰满度；F、待漆膜做出丰满度后，哑光面漆甲、乙、丙组份按比例开稀后，通过喷/刷涂施工；G、待漆膜干燥后漆膜干燥后，通过层间打磨重涂来刷出漆膜丰满度；H、完成面漆涂刷后，应确保漆膜完成干燥前不受外界触碰。作为上述技术方案的改进，所述乙组份由正丁酯、HI-100或3390配制成。进一步，所述丙组份由正丁酯、丙二醇甲醚醋酸酯、四甲苯、MIBK和二甲苯配制成。进一步，所述甲组份、乙组份、丙组份、三个组份的质量配比为1：0.5～0.8：0.4～0.6。本专利技术的有益效果是：本专利技术的户外用木器涂装工艺，经检测和试用证明，其涂层附着力强、柔韧性好、硬度高、遮盖力好、高光泽，施工时流平性好，能显著提高漆膜涂装长期使用时的耐磨耐划性能，能够很好的满足户外使用环境。具体实施方式下面对本专利技术作进一步详细说明。双组份由涂料以及固化剂组成，固化剂能加速涂料成膜的速度，其中甲组份为主漆（封闭底漆、中涂底漆或者面漆），乙组份为固化剂，乙组份由正丁酯、HI-100或3390配制成，为调稀施工，还设置有丙组份，丙组份由正丁酯、丙二醇甲醚醋酸酯、四甲苯、MIBK和二甲苯配制成，不参与化学反应，经测试和试验，甲组份、乙组份、丙组份、三个组份的质量配比为1：0.5～0.8：0.4～0.6可以达到比较理想的效果。封闭底漆：本专利技术的一种双组份封闭底漆，按照质量比，包括如下成分：丙烯酸树脂78.7%～89.25%分散剂0.05%～0.2%流平剂0.1%～0.8%消泡剂0.1%～0.3%二甲苯1%～3%甲基异丁基酮1%～3%20%醋酸纤维素8%～12%醋酸正丁酯0.5%～2%上述成分混合后分散均匀至细度≤15um，粘度1500～2500mpa.s/25℃。实施例1：丙烯酸树脂78.7%Dispers610s分散剂0.05%Glide100流平剂0.3%EFKA-3600流平剂0.11%BYK-066N消泡剂0.3%二甲苯3%甲基异丁基酮3%20%醋酸纤维素12%醋酸正丁酯2%。实施例2：丙烯酸树脂89.25%Dispers610s分散剂0.05%Glide100流平剂0.05%EFKA-3600流平剂0.05%BYK-066N消泡剂0.1%二甲苯1%甲基异丁基酮1%20%醋酸纤维素8%醋酸正丁酯0.5%。实施例3：丙烯酸树脂83.5%Dispers610s分散剂0.2%Glide100流平剂0.3%EFKA-3600流平剂0.5%BYK-066N消泡剂0.2%二甲苯2%甲基异丁基酮2%20%醋酸纤维素10%醋酸正丁酯1.3%。中涂底漆：本专利技术的一种双组份中涂底漆，按照质量比，包括如下成分：饱和聚酯树脂44%～66.25%合成脂肪酸树脂15%～25%10%澎润土浆4%～6%分散剂0.5%～2%流平剂0.15%～0.5%消泡剂0.1%～0.3%二甲苯1%～3%硬酯酸锌2%～3.5%醋酸正丁酯0.5%20%醋酸纤维素8%～12%光稳定剂1%～2%醋酸正丁酯1.5%～3%上述成分混合后分散均匀至细度≤35um，粘度2500～3500mpa.s/25℃。实施例1：饱和聚酯树脂44%合成脂肪酸树脂25%10%澎润土浆6%Dispers610s分散剂2%EFKA-3600流平剂0.05%EFKA-3033流平剂0.1%BYK-066N消泡剂0.1%二甲苯1.75%硬酯酸锌3.5%醋酸正丁酯0.5%20%醋酸纤维素12%1130光稳定剂1%292光稳定剂1%醋酸正丁酯3%。实施例2：饱和聚酯树脂66.1%合成脂肪酸树脂15%10%澎润土浆4%Dispers610s分散剂0.5%EFKA-3600流平剂0.2%EFKA-3033流平剂0.1%BYK-066N消泡剂0.1%二甲苯1%硬酯酸锌2%醋酸正丁酯0.5%20%醋酸纤维素8%1130光稳定剂0.5%292光稳定剂0.5%醋酸正丁酯1.5%。实施例3：饱和聚酯树脂54.75%合成脂肪酸树脂20%10%澎润土浆5%Dispers610s分散剂1.5%EFKA-3600流平剂0.05%EFKA-3033流平剂0.1%BYK-066N消泡剂0.1%二甲苯2%硬酯酸锌3%醋酸正丁酯0.5%20%醋酸纤维素10%1130光稳定剂0.5%292光稳定剂0.5%醋酸正丁酯2%。面漆：本专利技术的一种双组份哑光面漆，按照重量比，包括如下成分：丙烯酸树脂66.2%～79.55%聚乙烯蜡浆1%～2%分散剂0.5%～0.2%流平剂0.5%～0.5%消泡剂0.1%～0.3%二甲苯2%～4%消光粉4.2%～5.8%醋酸正丁酯0.5%20%醋酸纤维素8%～12%20%聚酰氨蜡2.5%～3.5%光稳定剂1%～2%醋酸正丁酯0.5%～3%分散均匀至细度≤15um，粘度2000～3000mpa.s/25℃。实施例1：丙烯酸树脂66.2%4200-10聚乙烯蜡浆2%Dispers610s分散剂0.2%EFKA-3600流平剂0.2%EFKA-3033流平剂0.2%BYK-066N消泡剂0.3%二甲苯4%消光粉5.8%醋酸正丁酯0.5%20%醋酸纤维素12%20%聚酰氨蜡3.5%1130光稳定剂1%292光稳定剂1%醋酸正丁酯3%实施例2：丙烯酸树脂79.55%4200-10聚乙烯蜡浆1%Dispers610s分散剂0.5%EFKA-3600流平剂0.05%EFKA-3033流平剂0.1%BYK-066N消泡剂0.1%二甲苯2%消光粉4.2%醋酸正丁酯0.5%20%醋酸纤维素8%20%聚酰氨蜡2.5%1130光稳定剂0.5%292光稳定剂0.5%醋酸正丁酯1%实施例3：丙烯酸树脂74.1%4200-10聚乙烯蜡浆1.5%Dispers610s分散剂0.4%EFKA-3600流平剂0.1%EFKA-3033流平剂0.2%BYK-066N消泡剂0.2%二甲苯3%消光粉5%醋酸正丁酯0.5%20%醋酸纤维素10%20%聚酰氨蜡3%1130光稳定剂0.75%292光稳定剂0.75%醋酸正丁酯0.5%在本专利技术中，所述20%醋酸纤维素通过如下方法制备：将20%甲乙酮、20%的CAB-551-0.2以及60%的本文档来自技高网...

【技术保护点】
一种户外木器涂装工艺，其特征在于，包括如下步骤：确保木材含水率＜10%；封闭底漆按甲、乙、丙组份按比例开稀；通过喷/刷涂施工，先用封闭底漆对白坯完全封闭两遍；待漆膜干燥后，打磨清理干净后，中涂底漆甲、乙、丙组份按比例开稀后，通过喷/刷涂施工；待漆膜干燥后，通过层间打磨重涂来刷出漆膜丰满度；待漆膜做出丰满度后，哑光面漆甲、乙、丙组份按比例开稀后，通过喷/刷涂施工；待漆膜干燥后漆膜干燥后，通过层间打磨重涂来刷出漆膜丰满度；完成面漆涂刷后，应确保漆膜完成干燥前不受外界触碰。

【技术特征摘要】
1.一种户外木器涂装工艺，其特征在于，包括如下步骤：确保木材含水率＜10%；封闭底漆按甲、乙、丙组份按比例开稀；通过喷/刷涂施工，先用封闭底漆对白坯完全封闭两遍；待漆膜干燥后，打磨清理干净后，中涂底漆甲、乙、丙组份按比例开稀后，通过喷/刷涂施工；待漆膜干燥后，通过层间打磨重涂来刷出漆膜丰满度；待漆膜做出丰满度后，哑光面漆甲、乙、丙组份按比例开稀后，通过喷/刷涂施工；待漆膜干燥后漆膜干燥后，通过层间打磨重涂来刷出漆膜丰满度...

【专利技术属性】
技术研发人员：方学平，杨长春，严修才，
申请(专利权)人：广东花王涂料有限公司，
类型：发明
国别省市：广东;44