The invention relates to a cable conductor filled with graphene and a preparation method thereof. A cable conductor filler based on graphene, including single conductor, a plurality of single conductor stranded conductor formed body, gap is arranged between the adjacent single conductor, the gap is filled with graphene, a semi conductive nylon tape on the conductor outside of the package. The invention relates to a method for preparing the cable conductor, which comprises the following steps: firstly, a single wire conductor is prepared, and then the graphene is filled between the single wire conductors. The invention provides a single lower contact resistance, increase the conductivity, in the same conductor resistance requirements can save the conductor material, a conductor and a preparation method of graphene filled on the same section of conductor can greatly improve the electric performance and carrying capacity; solve the cable conductor resistance existing in the prior art the large, low conductivity problem.
【技术实现步骤摘要】
本专利技术涉及一种电缆导体,尤其涉及一种填充有石墨烯的电缆导体及其制备方法。
技术介绍
电缆二类导体均采用多根绞合,为了增加导体性能和减少电缆外径,均会采用在绞线过程中进行分层紧压,使的导体紧压系数只能达到0.9及以上,但中间还是有很多空隙填充了空气,影响导体电阻,目前,各大电缆厂都没有找到很好的材料和方法来填充其空隙以提高其导电性能,,如果采用实心导体就不能满足电缆的柔软性能。导体空隙会增大接触电阻,进而影响导体电阻;导体缝隙不能填充,导体外圆形状不规则,生产中压电缆时绝缘或导体屏蔽容易变形,造成电场畸变,产生质量隐患。如中国专利:一种含石墨烯的橡胶绝缘电缆(CN202307250U),包括铜导体,所述铜导体外同心包裹有石墨烯层和绝缘橡胶层,外圈包覆有护套。但是该结构同样没有注意到导体之间的间隙问题。
技术实现思路
本专利技术提供了一种降低单丝接触电阻,提高导电性能,在同一导体电阻要求下可节约导体材料,相同截面导体时大大提高其电性能及承载能力的一种基于石墨烯填充的电缆导体及其制备方法;解决了现有技术中存在的电缆导体电阻大,导电性能低的技术问题。本专利技术的上述技术问题是通过下述技术方案解决的:一种基于石墨烯填充的电缆导体,包括单丝导体,多根单丝导体绞合形成导体本体,相邻单丝导体之间设有缝隙,在缝隙内填充有石墨烯,在导体本体外包裹有半导电尼龙带。电缆导体是由多根单丝绞合而成的,即使对电缆导体进行紧压,依然会在各个单丝导体之间存在间隙,为了提高导电性能,在间隙内填充有石墨烯,石墨烯具有良好的导电性能,并且电阻率低,质量轻薄,在同一导体电阻要求下可节约导体材料, ...
【技术保护点】
一种基于石墨烯填充的电缆导体,其特征在于:包括单丝导体,多根单丝导体绞合形成导体本体,相邻单丝导体之间设有缝隙,在缝隙内填充有石墨烯,在导体本体外包裹有半导电尼龙带。
【技术特征摘要】
1.一种基于石墨烯填充的电缆导体,其特征在于:包括单丝导体,多根单丝导体绞合形成导体本体,相邻单丝导体之间设有缝隙,在缝隙内填充有石墨烯,在导体本体外包裹有半导电尼龙带。2.根据权利要求1所述一种基于石墨烯填充的电缆导体,其特征在于:所述的单丝导体为铜单丝。3.根据权利要求1或2所述一种基于石墨烯填充的电缆导体,其特征在于:所述的单丝导体的外圆周表面为粗糙表面。4.根据权利要求1或2所述一种基于石墨烯填充的电缆导体,其特征在于:在所述的单丝导体外包裹有石墨烯层。5.一种如权利要求1所述的电缆导体的制备方法,其特征在于:第一步,制备单丝导体:在拉丝机上拉制出所需直径的单丝,将拉好的单丝绕在线盘上;第二步,填充石墨烯:将拉好的单丝由上至下导入绞线机内...