The invention relates to an organic macromolecule composite material, and more specifically to a manufacturing process of a high electrical property warpage-resistant deformation PBT material, which is composed of the following components according to weight ratio: PBT: 80 90%; SMA: 1 3%; halogen-free mica microchip: 5 15%; halogen-free glass microsphere: 5 10%; toughening agent: 3 5%; coupling agent: 0.1 1.0%; other additives: 0.1 5.5%; original hair. The manufacturing process of a kind of PBT material with high electrical property and anti-warping deformation adds anti-warping deformation and high electrical property on the basis of excellent comprehensive mechanical property, and does not contain halogen. It is convenient to produce and purchase, and also meets all other environmental protection requirements, thus improving the comprehensive competitiveness.
【技术实现步骤摘要】
高电性能防翘曲变形PBT材料制作工艺
本专利技术涉及一种有机高分子复合材料,更具体地说,是涉及一种高电性能防翘曲变形PBT材料制作工艺。
技术介绍
PBT是目前应用最多的几种工程塑料之一,他拥有良好的成型加工性,结晶速度快,制品表面光泽好,尺寸较稳定,吸水率较低,耐化学品和耐油性优良,特别是耐电弧性优良,为其他工程塑料所不及,这些综合特点使其被广泛用于电气电子汽车机械仪器仪表等行业做结构件。但是随着社会发展,各项技术日新月异,PBT树脂的电性能优异特点已经在较多领域不能满足产品要求,并且越来越复杂的结构设计,也要求原材料具备更好的尺寸稳定性和成型加工性。因此,展开了对PBT进行复合改性的研究。而目前欧美/日本等等发达国家出于种种原因,掀起了对外国进口产品种种限制,设立了一系列的壁垒,其中,对电子电器产品的材质无卤要求,就是其中之一。本技术专利技术就是为了有效克服这种现象而产生的。
技术实现思路
本专利技术的目的在于有效的克服了现有技术的缺陷,提供一种材质不含卤且综合机械性能保持良好的基础上增加了防翘曲变形好和高电性能的高电性能防翘曲变形PBT原料。本专利技术提供的技术方案如下:本专利技术的一种高电性能防翘曲变形PBT原料是由以下成分按重量比组成,PBT:80-90%;SMA:1-3%;无卤云母微片:5-15%;无卤玻璃微珠:5-10%;增韧剂:3-5%;偶联剂:0.1-1.0%;其他助剂:0.1-5.5%。本专利技术所述的高电性能防翘曲变形PBT材料的制备方法,包括如下步骤:先将PBT烘干,无卤云母微片按照55度预热,然后将烘干后的PBT、SMA、无卤玻璃微珠 ...
【技术保护点】
1.一种高电性能防翘曲变形PBT材料制作工艺,其特征在于:是由以下成分按重量比组成,PBT:80‑90%;SMA:1‑3%;无卤云母微片:5‑15%;无卤玻璃微珠:5‑10%;增韧剂:3‑5%;偶联剂:0.1‑1.0%;其他助剂:0.1‑5.5%。
【技术特征摘要】
1.一种高电性能防翘曲变形PBT材料制作工艺,其特征在于:是由以下成分按重量比组成,PBT:80-90%;SMA:1-3%;无卤云母微片:5-15%;无卤玻璃微珠:5-10%;增韧剂:3-5%;偶联剂:0.1-1.0%;其他助剂:0.1-5.5%。2.一种高电性能防翘曲变形PBT材料制作工艺,其特征在于:包括...