The invention belongs to the technical field of manganese-zinc ferrite core, and discloses a method of diamond wire cutting, which is characterized by the following steps: first, placing cushion plate before cutting; placing resin strip, using aluminium-containing resin strip for viscose, using alcohol and alumina powder to clean the product; curing the viscose product; and wire cutting, which can directly retreat after cutting the product. Wire, semi-automatic cutting off products; using special water tank, automatic direct degumming of diamond products; WEDM products are finished. Wire-cut products have good dimensional consistency, save manpower and material resources, meet production requirements and improve work efficiency.
【技术实现步骤摘要】
一种金刚石线切割方法
本专利技术属于锰锌铁氧体磁芯
,具体地涉及金刚石线切割方法。
技术介绍
在锰锌软磁铁氧体的生产过程中,部分厚度尺寸薄、生产难度高的产品需要金刚石线切割,金刚石线切割是一道重要的工序,金刚石线切割的工艺比较复杂,步骤多,操作繁,难度大。如图1所示,金刚石线切割过程中,首先要进行粘胶,粘胶后固化,固化2小时以上,上机进行金刚石线切割,切割后的产品取下来,手工进行刮胶,最后清洗后待用。原有的金刚石线切割工艺采用大理石板进行粘胶,切好的产品用手掰下来,手工取下产品,掰下来的产品还需要人工刮胶,不仅费时费力,浪费人工,还对产品的尺寸和质量有影响。针对产品在金刚石线切割过程中的浪费人工,品质不良等问题,不断进行研究和改进,通过一系列的试验,研究出一种新的金刚石线切割方法,采用含铝树脂条粘胶,金刚石线切割后,产品在机器上直接退线,整板放入到水槽中,整齐的除胶,节省人力物力,达到生产的要求。
技术实现思路
本专利技术旨在克服现有技术的缺陷,针对上述问题,提供了一种金刚石线切割方法。采用该方法,在产品金刚石线切割时,使线切割后的产品尺寸一致性好,同时节省人力物力,满足生产要求,提升了工作效率。为了解决上述技术问题,本专利技术提供以下技术方案:一种金刚石线切割方法,其特征在于,包括以下步骤,首先切割前放置垫板;放置树脂条,采用含铝树脂条进行粘胶,使用酒精和氧化铝粉对产品进行清洁;对粘胶后的产品进行固化处理;线切割,在产品切割后可直接退线,半自动下料取下产品;采用专用水箱,对金刚石产品自动直接除胶;线切割产品。优选的,整板金刚石产品放入到水箱槽中。与现有 ...
【技术保护点】
1.一种金刚石线切割方法,其特征在于,包括以下步骤,首先切割前放置垫板;放置树脂条,采用含铝树脂条进行粘胶,使用酒精和氧化铝粉对产品进行清洁;对粘胶后的产品进行固化处理;线切割,在产品切割后可直接退线,半自动下料取下产品;采用专用水箱,对金刚石产品自动直接除胶;线切割产品。
【技术特征摘要】
1.一种金刚石线切割方法,其特征在于,包括以下步骤,首先切割前放置垫板;放置树脂条,采用含铝树脂条进行粘胶,使用酒精和氧化铝粉对产品进行清洁;对粘胶后的产品进行固化处理;线切割,在...