The invention discloses a method for manufacturing hot melt glass, the glass dielectric opening into the appropriate specifications, preparation of ceramic mould, which is characterized in that it comprises the following process: the required specifications of glass flat on the ceramic mold, the roller kiln in gas heating, heating, cooling to can be released in roller kiln. In the roller kiln, heating and cooling are carried out to the baking process for 80-120 minutes. Manufacturing method of decorative glass melt by the method has the advantages of low cost, high rate of finished products, energy saving, increase revenue, and the advantages of mass production.
【技术实现步骤摘要】
本专利技术涉及一种热熔玻璃的生产方法,具体是涉及传统的玻璃深加工成热熔玻璃的制造工艺方式。
技术介绍
传统的热熔装饰玻璃生产工艺流程主要是将玻璃片开介成适用的规格后,平放在用钢铁做成的模具上,再放进电焗炉内加温制玻璃软化的温度,使玻璃软化后按模具的图案自然成形后,再由电焗炉自然降温,整个生产过程需要7-8小时,这样生产工艺方式既耗时,又耗能大,而且钢模具的造价比较高,而且使用电焗炉温差大,产量低,产品质量不够保证,收成率又低,由于生产成本高,在市场上缺乏竞争力。
技术实现思路
本专利技术的目的在于提供一种成本低、产品的成品率高,节能降耗、增收节支,且可大批量生产的热熔装饰玻璃的制造方法。本专利技术是通过下述方法来实现上述目的的该热熔装饰玻璃的制造方法如下;首先将玻璃片开介成所需的规格,制备陶瓷砖坯模具,将所需规格玻璃平放在陶瓷砖坯模具上,将之放入辊道窑中,在辊道窑内进行加温、降温至出炉即可。辊道窑内进行加温、降温至出炉整个过程时间为80-120分钟。本专利技术的优点在于将原来传统使用热热熔玻璃钢模具改用为陶瓷坯模具,代替了钢模具造价高、笨重、生产过程中散热慢,影响产品质量的落后现象,取而代之的陶瓷坯模具,造价低,容易加工、轻巧、且在生产过程中散热快、产品变形小,收成率高,并可以循环多次使用。该工艺方法在原来传统运用电焗炉的生产的方式上,改革创新为使用燃气的辊道窑生产,辊道窑的生产优点在于可连续不间断地生产,炉温自动控制,产品从进炉、升温到降温、产品出炉,全过程温度可以自动控制,每炉产品的生产过程只需80-120分钟,而且生产效率高,产品的产量大,质量好,收 ...
【技术保护点】
一种热熔玻璃的制造方法,首先将玻璃片开介成适当的规格,制备模具,其特征在于,所述模具为陶瓷坯模具,它还包括如下工艺:将所需规格玻璃平放在陶瓷坯模具上,将之放入辊道窑,在辊道窑内进行加温、降温至出炉即可。
【技术特征摘要】
【专利技术属性】
技术研发人员:陈利承,陈佳伟,丁雄,
申请(专利权)人:陈利承,
类型:发明
国别省市:44[中国|广东]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。