一种水性聚氨酯防水涂料制造技术

本发明专利技术公开了一种水性聚氨酯防水涂料，它是由下述重量份的原料组成的：水性聚氨酯树脂40-50、乙二醇乙醚醋酸酯5-8、聚四氟乙烯20-30、阳起石粉10-15、偏硅酸钠2-3、十二烷基磺酸钠1-2、聚四氢呋喃醚二醇2-3、十二烷基三甲基氯化铵1-2、去离子水5-10、粘结助剂7-10，本发明专利技术生产的防水涂料无毒无味，无污染环境，绿色环保，耐侯性好，高温不流淌，低温不龟裂，有很好的耐老化性，断裂伸长率高，防水效果好。

Water based polyurethane waterproof coating

The present invention discloses a kind of waterborne polyurethane waterproof coating, it is composed of the following raw materials: aqueous polyurethane resin 40-50, ethylene glycol monomethyl ether 5-8, Teflon 20-30, actinolitic powder 10-15, sodium metasilicate, sodium dodecyl sulfate 2-3 twelve 1-2, four 2-3, twelve hydrogen furan glycol ether three alkyl ammonium chloride 1-2, deionized water 5-10, bonding agent 7-10, the production of waterproof coating non-toxic and tasteless, no pollution, green environmental protection, good weather, no flow under high temperature, low temperature cracking, good ageing resistance, high elongation, good waterproof effect.

【技术实现步骤摘要】

【技术保护点】
一种水性聚氨酯防水涂料，其特征在于它是由下述重量份的原料组成的：水性聚氨酯树脂40?50、乙二醇乙醚醋酸酯5?8、聚四氟乙烯20?30、阳起石粉10?15、偏硅酸钠2?3、十二烷基磺酸钠1?2、聚四氢呋喃醚二醇2?3、十二烷基三甲基氯化铵1?2、去离子水5?10、粘结助剂7?10；所述的粘结助剂是由下述重量份的原料组成的：聚醋酸乙烯乳液30?40、聚乙烯醇6?10、三七粉2?3、卡波树脂4?6、N?乙基?邻、对甲苯磺酰胺0.5?1、硅铝酸钠2?3、水适量；将上述硅铝酸钠与聚乙烯醇混合，预热到30?40℃，球磨10?15分钟，加入到该混合料重量3?5倍的水中，加热到75?85℃，充分搅拌，加入三七粉、卡波树脂，升高温度为100?120℃，搅拌至温度为25?30℃，加入剩余各原料，充分球磨，即得所述粘结助剂。

【技术特征摘要】

【专利技术属性】
技术研发人员：鲁明，
申请(专利权)人：芜湖杰诺科技有限公司，
类型：发明
国别省市：