一种高附着力环氧树脂粉末涂料制造技术

本发明专利技术公开了一种高附着力环氧树脂粉末涂料，它是由下述重量份的原料组成的：E-51环氧树脂50-60、二亚乙基三胺6-10、贝壳粉3-5、六方氮化硼4-5、双酚a二缩水甘油醚2-3、浮花剂0.1-2、氧化亚铜2-3、锌粉1-2、超细硫酸钡10-12、N,N,N',N'-四(2-羟乙基)己二酰胺1-2、聚氯乙烯2-4、复合填料4-10；本发明专利技术的粉末涂料安全无毒副作用，环保性好，装饰效果好，具有很好的硬度和抗污染性，综合性能优越。

Epoxy resin powder paint with high adhesion

The invention discloses a high adhesion of epoxy resin powder coating, which is composed of the following raw materials: E-51 epoxy resin 50-60, two 6-10, three ethylene amine shell powder 3-5, six 4-5, two BN bisphenol A diglycidyl ether 2-3, embossing agent 0.1-2, 2-3, 1-2, zinc oxide ultrafine barium sulfate 10-12, N, N, N', N'- four (2- hydroxyethyl) has two amide 1-2, 2-4 PVC, 4-10 composite filler of the invention has no toxic side effect; powder coating safety, good environmental protection, good decorative effect, has good hardness and anti pollution, comprehensive performance.

【技术实现步骤摘要】

【技术保护点】
一种高附着力环氧树脂粉末涂料，其特征在于它是由下述重量份的原料组成的：E?51环氧树脂50?60、二亚乙基三胺6?10、贝壳粉3?5、六方氮化硼4?5、双酚a二缩水甘油醚2?3、浮花剂0.1?2、氧化亚铜2?3、锌粉1?2、超细硫酸钡10?12、N,N,N“,N“?四(2?羟乙基)己二酰胺1?2、聚氯乙烯2?4、复合填料4?10；所述的复合填料是由下述重量份的原料组成的：红土40?45、聚四氟乙烯6?8、乙酰丙酮铝2?3、二硼化钒1?2、N,N?亚甲基双丙烯酰胺0.6?1、三羟甲基丙烷1?2；将上述红土在600?800℃下煅烧3?5小时，加入聚四氟乙烯，球磨混合1?2小时，将三羟甲基丙烷加热到55?60℃后加入，混合均匀，加入剩余各原料，400?600转/分搅拌分散20?25分钟，烘干，充分球磨，即得所述复合填料。

【技术特征摘要】

【专利技术属性】
技术研发人员：万鹏程，马千里，徐磊，徐曙，代宝成，
申请(专利权)人：安徽明都电气有限公司，
类型：发明
国别省市：