The invention relates to a slurry process of an electrode slurry of a lithium ion battery, belonging to the electrochemical technology field. The process comprises the following steps: dilute binder, stirring speed of 5 ~ 20 R / min, stirring for 10 to 50 minutes; adding conductive agent, stirring speed of 5 ~ 20 R / min, stirring for 10 to 50 minutes; the active material is divided into three or more times with each barrel, adding active material, stirring speed of 10 ~ 25 R / min, stirring for 5 to 30 minutes; with the liquid pump slurry to ultrasonic equipment for ultrasonic dispersion, liquid pump outlet pressure is 0.05 ~ 1.0MPa, ultrasonic frequency 1 ~ 10kHz, the slurry after ultrasonic treatment directly into the coating machine for coating. The invention mainly uses ultrasonic cavitation slurry, the slurry after ultrasonic treatment directly into the coating machine, simplify the process, greatly improving the production efficiency, improve the uniformity and stability of slurry and coating quality.
【技术实现步骤摘要】
本专利技术涉及一种锂离子电池电极浆料的合浆工艺，属于电化学
技术介绍
在锂离子电池生产中，电极浆料的均勻性、稳定性是关系到电池一致性、稳定性的 关键因素，是提高锂离子电池的安全性，减少因浆料团聚及涂布质量问题引起的微短路的 重要条件。优良的合浆方法不仅可以提高浆料的均勻性和稳定性，还可以提高生产效率和 原料的利用率，减少原料浪费，降低生产成本。因此，提高生产效率、提高浆料的均勻性和稳 定性成为所有电池企业非常关注的工艺要点之一。
技术实现思路
本专利技术的目的在于提供一种锂离子电池电极浆料的合浆工艺。为实现上述目的，本专利技术采用的技术方案是，一种锂离子电池电极浆料的合浆工 艺，先机械搅拌，然后超声波分散制备锂离子电池电极浆料，包括以下步骤(1)把粘结剂 与溶剂加入料桶中，公转速度5 20转/分钟，搅拌10 50分钟；(2)把导电剂加入料桶， 公转速度5 20转/分钟，搅拌10 50分钟；(3)把活性物质加入料桶，公转速度10 25转/分钟、分散速度200 2000转/分钟，搅拌5 30分钟，制成浆料；(4)将上述浆料 送入超声设备进行超声分散，超声波...
【技术保护点】
１．一种锂离子电池电极浆料的合浆工艺，其特征在于，先机械搅拌、然后超声波分散制备锂离子电池电极浆料，包括以下步骤：（１）将粘结剂与溶剂加入料桶中机械搅拌，搅拌速度５～２０转／分钟，搅拌１０～５０分钟；（２）把导电剂加入料桶，搅拌速度５～２０转／分钟，搅拌１０～５０分钟；（３）把活性物质加入料桶，搅拌速度１０～２５转／分钟、分散速度２００～２０００转／分钟，搅拌５～３０分钟，制成浆料；（４）将上述浆料送入超声设备进行超声分散，超声波频率１．０～１０ｋＨｚ。
【技术特征摘要】
【专利技术属性】
技术研发人员：鲁桂梅，
申请(专利权)人：中航锂电洛阳有限公司，
类型：发明
国别省市：41