The invention provides a local thermal aging and vibration assisted local thermal aging method, this method is mainly based on the materials of parts, structural geometry, pre processing and processing parameters, through experience or computer modeling of virtual manufacturing technology to the needs of aging parts of internal elastic properties, residual stress distribution was analyzed and determined the stress concentration region of process parameters; then according to the parameters of aging treatment combined with thermal aging or thermal aging and vibration aging on parts. The present invention achieves the purpose of removing residual stress and homogenizing tissue by means of local thermal aging and vibration assisted local thermal aging method. Compared with the traditional heat aging and vibration aging technology, this method not only can make effective use of energy, energy conservation, improve the aging effect, and decrease in local heating to reduce parts of natural frequency of vibration aging makes noise.
【技术实现步骤摘要】
本专利技术涉及一种时效处理消除零部件残余应力的方法。
技术介绍
铸造、锻造、轧制、焊接等制造工艺以及车、削、铣、磨、钻等机械加工工艺都可能在 金属零部件的内部产生不同程度的残余应力。在后续加工或使用过程中，这类零部件的残 余应力会因环境的变化自行释放，从而影响零部件的尺寸精度和使用性能。因此，对有一定 精度要求的零部件，在其成为终成品之前需要进行时效处理，以去除和均化其残余应力。时效方法可以分为自然时效和人工时效两大类。工程上应用最为广泛的人工时效 方法是热时效和振动时效。热时效方法是将零部件按照一定的升温曲线加热到指定温度并保持一段时间，然 后再按照一定的降温曲线将零部件的温度降至室温。对于钢制零部件需要保温数小时，甚 至更长时间，使其内部的残余应力充分释放。因为是整体加热、且加热的时间和温度可以精 确控制，热时效方法可以有效调控零部件内部残余应力的消除程度和均化水平。但是，由于 会明显降低零部件材料的力学性能和结构刚度，热时效方法不适宜于材料性能和结构刚度 要求高的零部件，譬如薄壁钢结构件和铝合金、钛合金等轻合金材料制造的零部件。此外， 用热时效方法处理零...
【技术保护点】
１．一种局部热时效和振动辅助局部热时效的方法，其特征为，具体包括如下步骤：１）根据零件材质、结构几何、前期加工和处理工艺等参数，通过经验判断或计算机建模虚拟制造技术对需要进行时效处理的零部件内部弹性能、残余应力分布进行分析，确定其应力分布集中区域等工艺参数；２）通过由步骤１）中分析结果，从下面三个时效处理方法中选择一种对零件进行处理：当零部件性能或结构特征不适合振动时效时，只对零件进行局部热时效；当零部件材料在加热之后其固有频率得到显著下降，而撤销热源后其固有频率大幅回升时，使用局部热时效与整体振动时效同时进行的方法对零件进行时效处理；当零部件材料在加热之后其固有频率得到显...
【技术特征摘要】
【专利技术属性】
技术研发人员：陈光南，张坤，彭青，何伶荣，吴臣武，王明星，肖京华，罗耕星，
申请(专利权)人：中国科学院力学研究所，
类型：发明
国别省市：11