本发明专利技术涉及一种氧化锆陶瓷材料的制备方法。本发明专利技术所要解决的技术问题是提出一种新的氧化锆陶瓷材料的制备方法，该方法中的成型工序在室温条件下就可进行，有机塑化剂和水的用量也比较少；而且降低了烧结温度。解决该问题的技术方案是：本制备方法包括配料、挤出和烧结三大步骤，制备过程中添加膨润土作塑化剂，纤维素溶液作粘结剂，而且采用了挤出成型的技术。本发明专利技术可用于氧化锆陶瓷材料的生产制造领域。

Process for preparing zirconium oxide ceramic material

The invention relates to a preparation method of zirconia ceramic material. The technical problem to be solved is to put forward a new method of preparation of zirconia ceramic material, the forming process of this method at room temperature can be carried out, organic plasticizer and the amount of water is relatively small; and reduce the sintering temperature. The solution is: the preparation method comprises the steps of proportioning, sintering and extrusion of three steps in the preparation process of bentonite as plasticizing agent, cellulose solution as the binder, and the use of extrusion molding technology. The invention can be used in the field of the production of zirconia ceramic materials.

【技术实现步骤摘要】

本专利技术涉及，适用于氧化锆陶瓷材料的生产制造 领域。
技术介绍
由于氧化锆陶瓷具有高韧性、高抗弯强度和高耐磨性，优异的隔热性能，热膨胀系 数接近于钢等优点，因此被广泛应用于结构陶瓷领域。主要有=Y-TZP磨球、分散和研磨介 质、喷嘴、球阀球座、氧化锆模具、微型风扇轴心、光纤插针、光纤套筒、拉丝模和切割工具、 耐磨刀具、表壳及表带、高尔夫球的轻型击球棒及其它室温耐磨零器件等。同时在功能陶瓷方面，由于其优异的耐高温性能，作为感应加热管、耐火材料、发 热元件使用。氧化锆陶瓷具有敏感的电性能参数，主要应用于氧传感器、固体氧化物燃料电 池(Solid Oxide Fuel Cell, SOFC)和高温发热体等领域。具有较高的折射率(N = 2. 1 2. 2)，在超细的氧化锆粉末中添加一定的着色元素(V2O5，Mo03，Fe203等)，可将它制成 多彩的半透明多晶&02材料，像天然宝石一样闪烁着绚丽多彩的光芒，可制成各种装饰品。 另外，氧化锆在热障涂层、催化剂载体、医疗、保健、耐火材料、纺织等领域正得到广泛应用。随着氧化锆陶瓷材料应用的越来越广泛，对这种陶瓷材料的批量化制备方面就提本文档来自技高网...

【技术保护点】
一种氧化锆陶瓷材料的制备方法，其特征在于包括以下步骤：ａ、配料：在练泥机上将氧化锆粉体、膨润土粉体和浓度为１～４％的纤维素溶液均匀混合，得到泥料，所述各原料占总原料量的重量百分比为：氧化锆粉体９３～９４％，膨润土粉体０．１～３％，纤维素溶液３～６％；ｂ、挤出：在挤出机中将步骤ａ得到的泥料进行挤出成型，挤出压力为０．５～１．０ＭＰａ，得到预期形状的素坯；ｃ、烧结：将步骤ｂ得到的素坯在高温炉中进行无压烧结，烧结温度为１３５０～１６００℃，保温时间为２～５ｈ，然后随炉冷却。

【技术特征摘要】

【专利技术属性】
技术研发人员：蒋丹宇，郑汉芳，徐兵，武光强，
申请(专利权)人：中国科学院上海硅酸盐研究所，杭州至卓通讯科技有限公司，
类型：发明
国别省市：31