A preparation method of a ceramic tile, which comprises the following steps: Step 1: the production of ceramic tile blank; step 2: making screen; step 3: glaze on biscuit; step 4: the glaze layer after drying, the product is placed in the kiln has the glaze glaze, which is made of ceramic tile. The invention adopts the special design of the screen, so the shade made of ceramic tile surface uneven color, at the same time, because the process of sequential design process in the two edition of glazed tile, led to the surface color of mutual penetration, glazed bright fatness. At the same time, the glaze and glaze powder formula of the invention is unique, and the use of metal minerals, plus special glaze firing temperature and time, resulting in the ceramic tile glaze fambe small bubbles scattered natural, facing the light, such as the emerald moist exudes light, more layered texture. Intoxicated people highly appreciate the value.
【技术实现步骤摘要】
本专利技术涉及一种瓷砖的制备方法，具体涉及一种。
技术介绍
瓷砖已经深入到千家万户，为广大消费者所接受。目前，市面上的瓷砖品牌非常 多，而且种类丰富，如常见的瓷砖种类按使用的材料和制作工艺分为马赛克、釉面砖、玻化 砖或称抛光砖，其中釉面砖是由瓷砖底坯和表面一层釉面构成，即在陶瓷土坯上施釉经过 高温高压烧制而成，由于增加了釉面，使得陶瓷更加美观，深受消费者喜爱，但存在着颜色 不自然，色泽单一、图案对比度低等不足。
技术实现思路
本专利技术的目的，在于提供一种与现有釉面砖相比，色泽独特，更加自然，更具有美 感，具有乡村风格的。本专利技术是这样实现的一种，包括以下步骤步骤1 以普通瓷砖为基材，清洁瓷砖表面，除去灰尘，油污，砂砾，制成瓷砖素坯；步骤2 网版制作将图案分成不同的基本颜色进行制作，制作时菲林出片要求图 案品质最低为175线、300分辨率，将菲林的药面向上，进行拉网上浆，在网内上浆3次，网外 上浆4次，制成网版；步骤3 在素坯上施釉，先浸渍或喷涂无光釉，然后再布干粉釉；步骤4 釉层干燥后，将已施釉制品置于窑中釉烧，即制成窑变瓷砖。更进一步的方案是步骤3中无光釉和...
【技术保护点】
１．一种窑变瓷砖的制备方法，其特征在于包括以下步骤：步骤１：以普通瓷砖为基材，清洁瓷砖表面，除去灰尘，油污，砂砾，制成瓷砖素坯；步骤２：网版制作：将图案分成不同的基本颜色进行制作，制作时菲林出片要求图案品质最低为１７５线、３００分辨率，将菲林的药面向上，进行拉网上浆，在网内上浆３次，网外上浆４次；步骤３：在素坯上施釉，先浸渍或喷涂无光釉，然后再布干粉釉；步骤４：釉层干燥后，将已施釉制品置于窑中釉烧，即制成窑变瓷砖。
【技术特征摘要】
【专利技术属性】
技术研发人员：徐素容，
申请(专利权)人：成都新西南艺术陶瓷有限公司，
类型：发明
国别省市：90[中国|成都]