The invention is a kind of low cost self leveling cement mortar, excluding redispersible emulsion, in Portland cement, rapid hardening cement and gypsum three-phase system based on mixed with zeolite powder, wollastonite powder, fly ash, to meet the needs of practical engineering. The zeolite powder, wollastonite powder and fly ash in the excitation of cement hydration products, not only has the self curing, crack resistance, and play a part instead of cement, the performance of self leveling cement mortar is superior to add a lot of self leveling mortar polymer powder. The performance and the cost is relatively low.
【技术实现步骤摘要】
本专利技术是一种水泥基自流平砂桨。
技术介绍
水泥基自流平砂浆是一种干粉预混砂浆,广泛用于住宅、医院、超市等公共建筑室内地面及轻工业地面找平。水泥基自流平砂浆在新拌状态下,具有流动性好,可6动找平,施工方便,硬化快等特点,硬化 后的水泥基自流平砂浆具有抗压抗折及粘结强度高,体积稳定性好的特点。采用水泥基自流平砂浆找平地 面施工,可大幅度提高施工效率与质量。目甜的水泥基自流平砂浆大都掺入大量的可分散乳胶粉,不仅成本很高,胶粉还会影响了各种水泥优 越性的发挥。
技术实现思路
本专利技术是一种低成本水泥自流平砂浆,不含可再分散乳胶,在硅酸盐水泥、快硬水泥和快硬石膏三相 体系基础上,掺用沸石粉、硅灰石粉、粉煤灰,满足实际工程需要。由于沸石粉、硅灰石粉、粉煤灰在水 泥水化产物的激发下,不但具有自养护、抗裂性,同时起到部分替代水泥的作用,使配制的水泥5流平砂 浆性能具有优越于加入大量聚合物胶粉的自流平砂浆的性能,而成本却相对较低。本专利技术利用天然矿物沸石粉提高自流平砂浆的自养护能力、改善体积稳定性,同时改善自流平砂浆的 和易性及施工性能。沸石粉是天然沸石岩矿经磨细而成,含有活性二氧化硅和三氧化二铝,在碱激发下,能与水泥水化的产物反应,促进水泥水化;沸石具有网格构状结构,内部充满大小均匀的孔穴和通道,掺 入砂浆中, 一方面,可吸收其中多余的拌和水,克服自流平砂浆泌水性,同时,自流平在凝结硬化过程中, 水泥水化继续需要水,被沸石粉吸附的水又能逐渐的释放出来起到自养护的作用。本专利技术利用主要成分是钙的偏硅酸盐的纤维状结构的天然矿物硅灰石,提高自流平砂桨的抗裂性、耐 磨性, ...
【技术保护点】
一种低成本水泥自流平砂浆,其特征在于材料的组成和含量(重量比例)为: 石英砂 30份 -40份 硅酸盐水泥 20-30份 快硬水泥 10-20份 硬石膏 4-8份 沸石粉 2-10份 硅灰 石粉 3-10份 粉煤灰 0-20份 减水剂 0.1-0.5份 缓凝剂 0.05-0.3份 消泡剂 0.05-0.2份。
【技术特征摘要】
1、一种低成本水泥自流平砂浆,其特征在于材料的组成和含量(重量比例)为石英砂 30份—40份硅酸盐水泥 20—30份快硬水泥 10—20份硬石膏 4—8份沸石粉 2—10份硅灰石粉 3—10份粉煤灰 0—20份减水剂 0.1—0.5份缓凝剂 0.05—0.3份消泡剂 0.05—0.2份2、 根据权利要求l所述的水泥基...
【专利技术属性】