The invention relates to an ultra transparent laminating film and its manufacturing method, the invention of the ultra transparent laminating film, followed by PVC (1) film, high transmittance acrylic pressure-sensitive adhesive (2), silicone release agent (3), PET (4) film, antistatic layer (5); the manufacture method the invention is carried out through the following steps: (1) the antistatic layer anilox stick coating, antistatic coating on the PET film, in 60 - 100 degrees Celsius oven, bake 1 to 2 minutes; (2) the use of silicon film machine silicone release agent coating finish in the first step; (3) in the coating machine, using transfer method: glue in the film, in 100 - 120 degrees Celsius in the oven to bake for 1 to 2 minutes, after drying glue and PVC film paste and together to complete the whole The beneficial effect of the invention is that the surface color and glossiness of the material which is protected by the mounting film is improved after the laminating treatment.
【技术实现步骤摘要】
本专利技术涉及一种裱膜，尤其涉及该裱膜的结构组成及其制造方法。
技术介绍
裱膜是一种拥有特殊功能的保护膜，在多种场合进行裱贴。 按使用分类，裱膜可以分为热裱膜和冷裱膜。现有技术中的冷裱膜有很多种，但是高透光率的裱膜还没有，因此很 多在需要裱膜场合的产品，它们的光泽度，透光率等出现问题，进而影响 到这些需要裱膜的产品的整体质量。主要表现在被裱膜保护的材料在裱膜 处理后，表面的色彩，光泽度等下降。
技术实现思路
本专利技术需要解决的技术问题是提供了一种超透裱膜，旨在解决上述问题；本专利技术还提供了制造该超透裱膜的方法。为了解决上述技术问题，本专利技术是通过以下技术方案实现的 本专利技术的超透裱膜包括依次为PVC膜、高透光率丙烯酸酯类压敏胶、 有机硅离型剂、PET膜、抗静电层；本专利技术的制造方法是通过以下步骤进行的1. 将抗静电层利用网纹棍涂布方式，将抗静电涂层涂在PET薄膜上，在摄氏60-100度的烘箱中，烘1-2分钟完成；2. 利用上硅机将有机硅离型剂涂布在第1步完成的薄膜上；3. 在涂布机上，利用转移法即上胶在离型膜上，在摄氏100-120度烘箱中烘1-2分钟...
【技术保护点】
一种超透裱膜，其特征在于：依次为ＰＶＣ膜（１）、高透光率丙烯酸酯类压敏胶（２）、有机硅离型剂（３）、ＰＥＴ膜（４）、抗静电层（５）。
【技术特征摘要】
1. 一种超透裱膜，其特征在于依次为PVC膜(1)、高透光率丙烯酸酯类压敏胶(2)、有机硅离型剂(3)、PET膜(4)、抗静电层(5)。2. 根据权利要求1所述的超透裱膜，其特征在于所述的PVC膜的厚度在35-120u之间；PET膜厚度在35-120u之间。3. —种制造超透裱膜的方法，是通过以下步骤进行的(1) .将抗静电层利用网纹棍涂布方式，将抗静电涂层涂在PET薄膜上，在摄氏60-100度的烘箱中，烘1-2分钟完成；(2) .利用上硅机将有机硅离型剂涂布在第1步完成的薄膜上；(3) .在涂布机上，利用转...
【专利技术属性】
技术研发人员：曹英杰，赵相生，
申请(专利权)人：上海丽源喷绘材料有限公司，上海山富数码喷绘复合材料有限公司，上海喜客标识材料有限公司，
类型：发明
国别省市：31[中国|上海]