The invention discloses a cryopreservation methods of inactivating preserved skull flap, (1) would have been out of the body's skull, kept at a low temperature, temperature not lower than 30 DEG C; (2) as skull repair materials, the skull flap in order to eliminate the natural thawing, live in saline water boiling; boiling time between 20 ~ 60 minutes. The processing method of the invention is able to process from the body's skull, preservation of its biological characteristics, finally use to other receptors; as a tool to replace expensive titanium alloy biomaterials, the majority of low-income people can be accepted; transplanted to recipient body, there is no inflammation and rejection and easily compatible with the receptor on the host tissue; skull flap was inactivated by boiling, formed by organic matter and calcium salt skeleton has not yet destroyed, provides conditions for bone regeneration, bone osteogenesis by surrounding normal bone and periosteum, gradually by creeping substitution and resurrection; without special equipment, economical and practical, especially for in basic level hospitals.
【技术实现步骤摘要】
本专利技术涉及人体组织脱离人体后的保存、处理方法，尤其是对颅骨进行摘取、保存、处理后作为组织移植物，使用到其他人体中，作为修补材料。
技术介绍
随着我国工农业和交通业的快速发展，重型颅脑损伤患者逐年快速增长。相当一部分患者因脑组织挫裂伤严重或肿胀明显或有脑疝形成而需要行去骨瓣减压术，需要将患者的骨瓣摘取下来；在进行减压手术后，即面临着颅骨修补的问题。而修补材料的选择是其中的主要环节之一。 当前异质材料的选择较多，主要有各种高分子材料和钛网等。异质材料由于无法被机体所吸收，存在排异和炎症反应，难与宿主组织相容，植入人体后周围毛细血管无法长入是产生感染的主要原因之一。如名称为生物活性钛材料及其制作方法、专利申请号为200810026377.9的专利技术专利所公开的生物活性钛材料，其由粒度为5 iim 100 iim的金属钛或钛合金粉等静压成形，在110(TC 130(TC真空烧结；粉末冶金烧结后的材料在乙酸钙、甘油磷酸钠和氢氧化物配置的电解水溶液中微弧氧化处理，制备得到生物活性钛材料；可用于制备人体骨骼和牙齿等硬组织用生物置换(修复)体。在另一名称为用作人工骨骼的钛...
【技术保护点】
低温保存灭活处理异体颅骨瓣的方法，其特征在于包括如下操作步骤：（１）将已经脱离人体的颅骨瓣，在低温下保存，保存温度不低于－３０℃；（２）需要作为颅骨修补材料时，将颅骨瓣自然解冻，在生理盐水中煮沸以灭活；煮沸时间在２０～６０分钟之间。
【技术特征摘要】
低温保存灭活处理异体颅骨瓣的方法，其特征在于包括如下操作步骤(1)将已经脱离人体的颅骨瓣，在低温下保存，保存温度不低于-30℃；(2)需要作为颅骨修补材料时，将...
【专利技术属性】
技术研发人员：曹冠柏，邓泽虎，王德树，刘先齐，陈文浩，黎勇夫，袁晓剑，
申请(专利权)人：曹冠柏，
类型：发明
国别省市：85[中国|重庆]