The pressure hollow cubic block for diamond synthesis, is divided into an inner chamber and an outer chamber two, external cavity for pyrophyllite powder, the inner formula of raw materials including silica 5% - 20%, 5% - 20%, three Magnesium Oxide two aluminum oxide 5% - 30%, 5 - 30% with calcium oxide, ferric oxide 1.5% - 30%, three oxidation two Ni 0.01%10%. After roasting and mixing, pressing and forming. The utility model can improve the heat preservation performance of the artificial diamond, the color is good, the transparency is high, the crystal shape is good, and the output of the single stick is high.
【技术实现步骤摘要】
本专利技术涉及人造金刚石合成工艺中的传压介质合成金刚石用的空心立方块。在我国人造金刚石行业合成工艺中,人造金刚石在传压介质空心立方块的内腔内成长。而以单一的叶腊石作为传压介质,是我国人造金刚石行业合成工艺中,几十年来从未更换过主要辅助材料。近几年来出现了白云石和叶腊石相结合而成的合成用空心立方块,其原材料取材于天然矿石非人工合成材料。但上述材料合成的空心立方块,保温性能一般,合成生产的人造金刚石颜色、透明度、晶形不理想,晶体内有气泡,含杂多且伴有裂纹。本专利技术的目的旨在提供一种可大大地提高其保温性能,使产出的人造金刚石颜色好,透明度高,晶形好、单棒产量高的人工合成的人造金刚石合成用传压介质空心立方块。本专利技术的目的是通过下述方式实现的(以重量计)本专利技术分内腔、外腔二层,外腔为叶腊石矿粉,其内腔原料配方包括二氧化硅5%-20%、氧化镁5%-20%、三氧化二铝5%-30%、氧化钙5-30%,加入三氧化二铁1.5%-30%,三氧化二镍0.01%-10%。其中三氧化二铁较适合的含量为1.5%-20%,三氧化二镍0.01%-5%。本专利技术最适合的含量为二氧化硅8%-20%、氧化镁8%-20%、三氧化二铝18%-30%、氧化钙18%-30%,加入三氧化二铁1.5%-10%,三氧化二镍0.01%-2%。本专利技术的内腔可制成浅红色或红色或深红色。附图为本专利技术的示意图。图面说明1-内腔 2-外腔将上述粉末状的内腔原料按一定配比称重,将二氧化硅、氧化镁、三氧化二铝、氧化钙焙烧后,再加入三氧化二铁、三氧化二镍混合,并与粘合剂充分搅拌后与叶腊石矿粉相结合通过 ...
【技术保护点】
一种人造金刚石合成用传压空心立方块,分内腔、外腔,其内腔原料配方包括二氧化硅5%-20%、氧化镁5%-20%、三氧化二铝5%-30%、氧化钙5-30%粉末状原料,其特征在于加入三氧化二铁1.5%-20%,三氧化二镍0.01%-10%,以重量计。
【技术特征摘要】
1.一种人造金刚石合成用传压空心立方块,分内腔、外腔,其内腔原料配方包括二氧化硅5%-20%、氧化镁5%-20%、三氧化二铝5%-30%、氧化钙5-30%粉末状原料,其特征在于加入三氧化二铁1.5%-20%,三氧化二镍0.01%-10%,以重量计。2.如权利要求1所述的一种人造金刚石合成用传压空心立方块,其特征在于其中三氧化二铁的含量为1.5%-20%,三氧化二镍0....
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。