A method of whitening decabromodiphenyl ether and its products, made of high purity two phenyl ether which adopts two phenyl ether without solvent after recrystallization of decabromodiphenyl ether; sodium hypochlorite or hydrogen peroxide bleach bleach decabromodiphenyl ether; modified whitening of decabromodiphenyl oxide with white fluorescent dye is added; can also be used for the non solvent recrystallization method made of decabromodiphenyl oxide after modification, modification or bleaching made whiteness greater than 94 of decabromodiphenyl oxide. The invention has the advantages of low energy consumption, simple equipment and easy operation. Low cost and no environmental pollution.
【技术实现步骤摘要】
本专利技术涉及高分子塑料阻燃剂，尤其是十溴二苯醚阻燃剂。十溴二苯醚被广泛应用高分子塑料阻燃，它常用的生产方法是用二苯醚和溴作原料，在催化剂存在下进行溴代反应后制得。但是，目前国内生产的十溴二苯醚，其色泽呈浅黄色或棕黄色，白度大都低于88，这样的色泽作为阻燃剂添加到高分子塑料中制成产品时影响产品色度的稳定性。本专利技术的目的是提供十溴二苯醚的增白方法及提供白度高的十溴二苯醚，并具有方法简单、能耗低、不增加环境污染等优点。实现本专利技术目的技术方案的第一种增白方法是将二苯醚用无溶剂结晶法重复结晶提纯，结晶温度为26～28℃，并采用常规溴代法将二苯醚溴代生成十溴二苯醚；第二种方法是将十溴二苯醚用漂白工艺漂白，其中次氯酸钠漂白工艺，其工艺参数为漂白液中含次氯酸钠有效氯浓度0．2～10克／升，PH值2～10，漂白温度＜=50℃，漂白时间0．5～48小时，十溴二苯醚∶漂白液=10．5～2．5(重量比)，漂白后水洗；过氧化氢漂白工艺其工艺参数为漂白液中含过氧化氢0．1～8克／升，PH值8～12，漂白温度40～130℃、漂白时间0．01～24小时，十溴二苯醚∶漂白液=10．...
【技术保护点】
一种十溴二苯醚的增白方法，其特征在于：二苯醚用无溶剂结晶法重复结晶提纯，结晶温度为２６～２８℃，并采用常规溴代法将二苯醚溴代生成十溴二苯醚。
【技术特征摘要】
1．一种十溴二苯醚的增白方法，其特征在于二苯醚用无溶剂结晶法重复结晶提纯，结晶温度为26～28℃，并采用常规代法将二苯醚溴代生成十溴二苯醚。2．一种十溴二苯醚的增白方法，其特征在于将十溴二苯醚用漂白工艺漂白；a次氯酸钠漂白工艺，其工艺参数为漂白液中含次氯酸钠有效氯浓度0．2～10克／升，PH值2～10，漂白温度＜=50℃，漂白时间0．5～48小时，十溴二苯醚∶漂白液-1∶0．5～2．5(重量比)，漂白后水洗；b过氢化氢漂白工艺其工艺参数为漂白液中含过氧化氢0．1-8克/升，PH值8～12，漂白温度40～130℃，漂白时间0．01-24小时，十溴二苯醚∶漂白液=1∶0．5～2 5(重量比)，漂合液中还含有稳定剂。3．一种十溴二苯醚的增白方法，其特征在于在十溴二苯醚中添加白色荧光染料进行改性。4.一种十溴二苯醚的增白方法，其特征在于a上述权利要求1的方法所生产的十溴二苯醚，...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。