A silicone modified acrylic wall paint and preparation method, it is the high polymer with organosilicon monomer, acrylate monomer, acrylic acid, emulsifier, initiator, distilled water was prepared by solution polymerization reaction as the main film-forming material with water, defoaming agent, preservative, dispersing agent, filler thickener, mixing. The coating is a water-based paint, has high weather resistance, excellent gloss, hardness, adhesion strength, surface hydrophobicity, long service life, and no \three wastes\ emission during production and use.
【技术实现步骤摘要】
本专利技术涉及涂料这一
,特别是一种。目前,我国最常用的建筑涂料可分为油性涂料和水性涂料两大系列。油性涂料含有甲醛、有机溶剂、苯系物和重金属等有害成分,且有机溶剂易燃,不但给施工带来诸多不便,且挥发到空气中会造成环境污染和材料浪费,产品也易粉化、变色、脱落、从而影响装饰效果。水性涂料虽可保护环境、节约能源,但目前国内市场上投放的涂料质量差、档次低,主要表现在光泽低、附着力差、不耐水洗、自洁性差、易褪色。有一项申请号为97105779.6的专利涉及丙烯酸硅涂料及其制备方法。该涂料由丙烯酸乳液、硅树脂、填料、成膜助剂、增稠剂、防水剂、分散剂、消泡剂、防腐剂和水组成。该涂料的主要缺点是耐候性仍不够强。本专利技术的目的在于针对上述现有技术的不足之处,提供一种生产和使用过程中无“三废”排放的高耐候性、高附着力、高疏水性、使用寿命长的环保型涂料及其制备方法。本专利技术是通过下述技术方案实现的该涂料是以硅丙乳液为主要成膜物,加入填料、分散剂、消泡剂、防腐剂、增稠剂、水制成。各成分之间的配比为硅丙乳液30-38、填料30-35、分散剂0.5-1、消泡剂0.1-0.2、防腐剂0.1-0.3、增稠剂1-2、水30-35。硅丙乳液的组成(重量%)是由有机硅单体5-8、丙烯酸酯单体8.6-10、加入丙烯酸1-6、引发剂0.6-1.6、乳化剂3-5、蒸馏水70-80通过溶液聚合反应而制得的高分子聚合物。本涂料的配制方法是按上述组分配比进行配料,在反应釜中加入蒸馏水加热到85-90度,滴入有机硅单体、丙烯酸酯单体、丙烯酸及引发剂、乳化剂,2-3小时滴加完毕,再保温1小时, ...
【技术保护点】
一种有机硅改性丙烯酸外涂料,其特征在于它的组分(重量%)含有:硅丙乳液30-38、填料30-35、分散剂0.5-1、消泡剂0.1-0.2、防腐剂0、1-0、3、增稠剂1-2、水30-35。硅丙乳液的组成(重量%)是由有机硅单体5-8、丙烯酸酯单体8.6-10、加入丙烯酸1-6、乳化剂3-5、引发剂0.6-1.6、蒸馏水70-80通过溶液聚合反应而制得的高分子聚合物。
【技术特征摘要】
1.一种有机硅改性丙烯酸外涂料,其特征在于它的组分(重量%)含有硅丙乳液30-38、填料30-35、分散剂0.5-1、消泡剂0.1-0.2、防腐剂0、1-0、3、增稠剂1-2、水30-35。硅丙乳液的组成(重量%)是由有机硅单体5-8、丙烯酸酯单体8.6-10、加入丙烯酸1-6、乳化剂3-5、引发剂0.6-1.6、蒸馏水70-80通过溶液聚合反应而制得的高分子聚合物。2.根据权利要求1所述的有机硅改性丙烯酸外墙涂料,其特征在于填料是由钛白粉、云母粉和重质碳酸钙或高岭土组成,它们之间的配比(重量%)为钛白粉40-50、云母粉10-15、重质碳酸钙或高岭土35-45。3.一种制备权利要求1所述的有机...
【专利技术属性】
技术研发人员:崔新荣,徐梅清,赵玉顺,崔志勇,彭家起,
申请(专利权)人:东营市渤海装饰有限责任公司,
类型:发明
国别省市:37[中国|山东]